SOUND-ABSORBING COMPOSITE AND ITS USE
The present invention relates to composite elements comprising a layer of open-cell, hard, isocyanate-based foam and at least one further layer of isocyanate-based foam, and to their use for sound absorption.
1 . A composite element comprising at least two layers, each with a thickness of at least 5 mm, of different isocyanate-based foams, each having a DIN 53420 density of 130 kg/m 3 and each having a DIN EN 826 compressive strength of 5 to 200 kPa at 10% compression, the densities and compressive strengths of the at least two layers being different, with at least one of the at least two layers having a DIN 53430 elongation at break of greater than 30%, and each having on average 75 to 98% of open cells to DIN ISO 4590-86, and which optionally have an adhesive bonding layer between the at least two layers, wherein
A) at least one of the at least two foam layers consists of an irreversibly thermoformable, hard isocyanate-based foam having a DIN 53420 density of 10-45 kg/m 3 and a DIN EN 826 compressive strength at 10% compression of 30-200 kPa, the foam layer A) obtained from the reaction of the components consisting of
i) a polyol component consisting of
a. 15-60 wt %, based on the total amount of the isocyanate-reactive components of the polyol component i), of a polyether polyol with 10-50 wt % ethylene oxide fraction, having a number-average equivalent weight of 500-2500 g/mol and a functionality of 2 to 8,
b. 30-70 wt %, based on the total amount of the isocyanate-reactive components of the polyol component i), of a polyether polyol having a number-average equivalent weight of 50-480 g/mol and a functionality of 2 to 8,
c. optionally a chain extender and/or a crosslinking agent,
d. 1 to 15 wt %, based on the total amount of the isocyanate-reactive components of the polyol component i), of water and optionally further a blowing agent,
e. 0.3 to 5 wt %, based on the total amount of the isocyanate-reactive components of the polyol component i), of a catalyst,
f) optionally an auxiliary and/or an adjuvant,
ii) and an isocyanate component comprising
g) 55 to 100 wt %, based on the isocyanate component ii), of difunctional diphenylmethane diisocyanate (MDI) having an isomer weight ratio of 4,4′-MDI to 2,4′-MDI of 1:1 to 7:1,
g) 0 to 45 wt %, based on the isocyanate component ii), of a higher homologue of diphenylmethane diisocyanate (MDI),
B) the at least two foam layers each have at least an average sound absorption of 20% at a layer thickness of 1 cm in the range of 315-6350 Hz to ISO 10543 (Kund's tube).
2 . A method for producing a sound-absorbing panel comprising utilizing the composite element according to claim 1 .