Rubber composition for tire, and pneumatic tire
Provided are a rubber composition for tires which provides both adhesion to fiber cords and conductivity even when an inexpensive conductive carbon black is used, and thus achieves a balanced improvement in conductivity, handling stability, fuel economy, elongation at break, adhesion to fiber cords, processability, and tire durability; and a pneumatic tire including the composition. The composition includes, per 100 parts by mass of a rubber component: 1.0-3.5 parts by mass of sulfur with an iron content of 30 ppm or less, calculated as the net sulfur content in the sulfur; and 0.5-15 parts by mass of conductive carbon black having a DBP of 300 ml/100 g or more and an iron content of 60 ppm or more, the composition having a total net sulfur content of 1.0-6.0 parts by mass per 100 parts by mass of the rubber component, and a volume resistivity of 1.0×10 8 Ω·cm or less.
1. A pneumatic tire, comprising
a component comprising a rubber composition for a tire,
the rubber composition comprising, per 100 parts by mass of a rubber component:
1.0 to 3.5 parts by mass of a sulfur with an iron content of 30 ppm or less, calculated as a net sulfur content in the sulfur; and
0.5 to 15 parts by mass of a conductive carbon black having a dibutyl phthalate oil absorption of 300 ml/100 g or more and an iron content of 60 ppm or more,
wherein the rubber composition has a total net sulfur content of 1.0 to 6.0 parts by mass per 100 parts by mass of the rubber component, and has a volume resistivity of 1.0×10 8 Ω·cm or less,
wherein the sulfur with an iron content of 30 ppm or less is an insoluble sulfur with an iron content of 30 ppm or less.
2. The pneumatic tire according to claim 1 ,
wherein the conductive carbon black has an iron content of 300 ppm or more, and
the rubber composition has a volume resistivity of 1.0×10 7 ·cm or less.
3. The pneumatic tire according to claim 1 ,
wherein the rubber composition comprises 1.6 to 8.0 parts by mass of zinc oxide per 100 parts by mass of the rubber component.
4. The pneumatic tire according to claim 1 ,
wherein the rubber composition has a total net sulfur content of 2.0 to 3.5 parts by mass per 100 parts by mass of the rubber component, and is for use as a rubber composition for a fiber cord topping.
5. The pneumatic tire according to claim 1 ,
wherein the component is a rubberized fiber cord component.
6. The pneumatic tire according to claim 5 ,
wherein the rubberized fiber cord component is at least one of a carcass and a jointless band.