Unoriented film

1. Unoriented film comprising at least 70 wt.% of an heterophasic propylene copolymer (RAHECO), said heterophasic propylene copolymer (RAHECO) comprises a matrix (M) being a random propylene copolymer (R-PP) and an elastomeric propylene copolymer (E) dispersed in said matrix (M), wherein the heterophasic propylene copolymer (RAHECO) has:

(a) a melt flow rate MFR 2 (230° C.) measured according to ISO 1133 in the range of 3.0 to 10.0 g/10 min,

(b) a melting temperature Tm determined by differential scanning calorimetry (DSC) in the range of 130 to 150° C.,

(c) a xylene cold soluble content (XCS) determined according ISO 16152 (25° C.) in the range of 25 to 50 wt. %,

(d) a comonomer content in the range of 10.0 to 13.5 wt. %,

wherein the xylene cold soluble content (XCS) of the heterophasic propylene copolymer (RAHECO) has:

(e) a comonomer content in the range of 21.6 to 30 wt.% and

(f) an intrinsic viscosity (IV) determined according to DIN ISO 1628/1, (in Decalin at 135 ° C.) in the range of 0.8 to below 2.0 dl/g, and

wherein the random propylene copolymer (R-PP):

(g) has a comonomer content in the range of 7.1 to 9.0 wt.%, and

(h) comprises at least two propylene copolymer fractions (R-PP1) and (R-PP2), wherein the first propylene copolymer fraction (R-PP1) has a comonomer content in the range of 2.0 to 6.0 wt %, and the second propylene copolymer fraction (R-PP2) has a comonomer content in the range of 8.0 to 11.0 wt.%,

wherein the comonomer content of the elastomeric propylene copolymer (E) is in the range of 30.0 to 36.0 wt. %, and

wherein said film has a thickness of 5 to 2,000 μm.

2. Unoriented film according to claim 1 , wherein

[R-PP]−[R-PP1]≧2.5, wherein

[R-PP] is the comonomer content [wt. %] of the random propylene copolymer (R-PP), and [R-PP1] is the comonomer content [wt. %] of the first propylene copolymer fraction (R-PP1).

3. Unoriented film according to claim 1 , wherein the comonomers of the random propylene copolymer (R-PP), the first propylene copolymer fraction (R-PP1) and the second propylene copolymer fraction (R-PP2) are ethylene and/or C 4 to C 12 α-olefin.

4. Unoriented film according to claim 1 , wherein said film has:

(a) a tensile modulus in machine direction measured on a cast film with a thickness of 130 μm according to ISO 527-3 at 23° C. and a cross head speed of 1 mm/min in the range of 100 to 250 MPa, and/or

(b) a relative total penetration energy (Wbreak) as determined by the “Dynatest” method according to ISO 7725-2 at 0° C. on a cast film with a thickness of 130 μm in the range of 10 to 50 J/mm.

5. Unoriented film according to claim 1 , wherein said film has:

(a) a transparency of at least 90%,

(b) a haze of below 6.0%, and/or

(c) a clarity of at least 92%, measured on a 50 μm cast film according to ASTM D1003-00.

6. Unoriented film according to claim 1 , wherein said film has a hexane soluble content determined according to FDA (section 177.1520) on a 100 μm cast film of below 8.0 wt. %.

7. Unoriented film according to claim 1 , wherein the heterophasic propylene copolymer (RAHECO) has been visbroken.

8. Unoriented film according to claim 7 , wherein the heterophasic propylene copolymer (RAHECO) prior to visbreaking is a heterophasic propylene copolymer (Pre-RAHECO) comprising a matrix (Pre-M) being a random propylene copolymer (Pre-R-PP) and an elastomeric propylene copolymer (Pre-E) dispersed in said matrix (Pre-M), said heterophasic propylene copolymer (Pre-RAHECO) has:

(a) a melt flow rate MFR 2 (230° C.) measured according to ISO 1133 in the range of 0.3 to 2.5 g/10 min, and

(b) a xylene cold soluble content (XCS) determined according ISO 16152 (25° C.) in the range of 25 to 50 wt. %,

wherein further the xylene cold soluble content (XCS) of the heterophasic propylene copolymer (Pre-RAHECO) prior to visbreaking has an intrinsic viscosity (IV) determined according to DIN ISO 1628/1, (in Decalin at 135° C.) in the range of 1.4 to below 2.5 dl/g.

9. Unoriented film according to claim 1 , wherein the unoriented film is a cast film or a blown film.

10. Process for producing an unoriented film according to claim 1 , comprising the steps of:

(a) producing in a multistage process comprising at least two reactors connected in series a heterophasic propylene copolymer (Pre-RAHECO) comprising a matrix (Pre-M) being a random propylene copolymer (Pre-R-PP) and an elastomeric propylene copolymer (Pre-E) dispersed in said matrix (Pre-M), wherein said heterophasic propylene copolymer (Pre-RAHECO) has:

(a1) a melt flow rate MFR 2 (230° C.) measured according to ISO 1133 in the range of 0.3 to 2.5 g/10 min, and

(a2) a xylene cold soluble content (XCS) determined according ISO 16152 (25° C.) in the range of 25 to 50 wt. %,

wherein further the xylene cold soluble content (XCS) of said heterophasic propylene copolymer (Pre-RAHECO) has an intrinsic viscosity (IV) determined according to DIN ISO 1628/1, (in Decalin at 135° C.) in the range of 1.4 to below 2.5 dl/g,

(b) visbreaking the heterophasic propylene copolymer (Pre-RAHECO) of step (a) obtaining a heterophasic propylene copolymer (RAHECO), said heterophasic propylene copolymer (RAHECO) has:

(b1) a melt flow rate MFR 2 (230° C.) measured according to ISO 1133 in the range of 3.0 to 10.0 g/10 min,

(b2) a melting temperature Tm determined by differential scanning calorimetry (DSC) in the range of 130 to 150° C.,

(b3) a xylene cold soluble content (XCS) determined according ISO 16152 (25° C.) in the range of 25 to 50 wt. %, and

(b4) a comonomer content in the range of 10.0 to 13.5 wt. %,

wherein the xylene cold soluble content (XCS) of the heterophasic propylene copolymer (RAHECO) of step (b) has:

(b5) a comonomer content in the range of 21.6 to 30 wt.% and

(b6) an intrinsic viscosity (IV) determined according to DIN ISO 1628/1, (in Decalin at 135° C.) in the range of 0.8 to below 2.0 dl/g,

wherein the random propylene copolymer (R-PP):

(b7) has a comonomer content in the range of 7.1 to 9.0 wt.%, and

(b8) comprises at least two propylene copolymer fractions (R-PP1) and (R-PP2), wherein the first propylene copolymer fraction (R-PP1) has a comonomer content in the range of 2.0 to 6.0 wt %, and the second propylene copolymer fraction (R-PP2) has a comonomer content in the range of 8.0 to 11.0 wt. % and

wherein the comonomer content of the elastomeric propylene copolymer (E) is in the range of 30.0 to 36.0 wt. %; and

(c) extruding said heterophasic propylene copolymer (RAHECO) of step (b) into a unoriented film.

11. Process according to claim 10 , wherein:

(a) in a first reactor propylene and ethylene and/or C 4 to C 12 α-olefin are polymerized obtaining a first propylene copolymer fraction (Pre-PP1),

(b) transferring said first propylene copolymer fraction (Pre-PP1) in a second reactor,

(c) polymerizing in said second reactor in the presence of the first propylene copolymer fraction (Pre-PP1) propylene and ethylene and/or C 4 to C 12 α-olefin obtaining a second propylene copolymer fraction (Pre-PP2), said first propylene copolymer fraction (Pre-PP1) and said second propylene copolymer fraction (Pre-PP2) form the matrix (Pre-PP),

(d) transferring said matrix (Pre-M) in a third reactor, and

(e) polymerizing in said third reactor in the presence of the matrix (Pre-M) propylene and ethylene and/or C 4 to C 12 α-olefin obtaining an elastomeric propylene copolymer (E), said matrix (Pre-M) and said elastomeric propylene copolymer (E) form the heterophasic propylene copolymer (Pre-RAHECO).

12. Process according to claim 11 , wherein unoriented film and/or the heterophasic propylene copolymer (RAHECO) has:

(a) a melt flow rate MFR2 (230° C.) measured according to ISO 1133 in the range of 3.0 to 10.0 g/10 min,

(b) a melting temperature Tm determined by differential scanning calorimetry (DSC) in the range of 130 to 150° C.,

(c) a xylene cold soluble content (XCS) determined according ISO 16152 (25° C.) in the range of 25 to 50 wt. %,

(d) a comonomer content in the range of 10.0 to 13.5 wt. %,

wherein the xylene cold soluble content (XCS) of the heterophasic propylene copolymer (RAHECO) has:

(e) a comonomer content in the range of 21.6 to 30 wt. % and

(f) an intrinsic viscosity (IV) determined according to DIN ISO 1628/1, (in Decalin at 135° C.) in the range of 0.8 to below 2.0 dl/g.

13. A heterophasic propylene copolymer (RAHECO) for improving the optical properties of an unoriented film, comprising a matrix (M) being a random propylene copolymer (R-PP) and an elastomeric propylene copolymer (E) dispersed in said matrix (M),

wherein further the heterophasic propylene copolymer (RAHECO) has

(a) a melt flow rate MFR 2 (230° C.) measured according to ISO 1133 in the range of 3.0 to 10.0 g/10 min,

(b) a melting temperature Tm determined by differential scanning calorimetry (DSC) in the range of 130 to 150° C.,

(c) a xylene cold soluble content (XCS) determined according ISO 16152 (25° C.) in the range of 25 to 50 wt. %,

(d) a comonomer content in the range of 10.0 to 13.5 wt. %,

wherein the xylene cold soluble content (XCS) of the heterophasic propylene copolymer (RAHECO) has

(e) a comonomer content in the range of 21.6 to 30 wt. % and

(f) an intrinsic viscosity (IV) determined according to DIN ISO 1628/1, (in Decalin at 135° C.) in the range of 0.8 to below 2.0 dl/g,

wherein the random propylene copolymer (R-PP)

(g) has a comonomer content in the range of 7.1 to 9.0 wt. % and

(h) comprises at least two propylene copolymer fractions (R-PP1) and (R-PP2), wherein the first propylene copolymer fraction (R-PP1) has a comonomer content in the range of 2.0 to 6.0 wt %, and the second propylene copolymer fraction (R-PP2) has a comonomer content in the range of 8.0 to 11.0 wt. %, wherein the comonomer content of the elastomeric propylene copolymer (E) is in the range of 30.0 to 36.0 wt. %; and wherein said improvement is determined by a haze of below 6.0%, wherein said film has a thickness of 5 to 2,000 μm and the haze is measured on a 50 μm cast film according to ASTM D1003-00.

14. The heterophasic propylene copolymer (RAHECO) according to claim 13 , wherein the unoriented film is a cast film or a blown film.