Polyacrylonitrile-based copolymer, polyacrylonitrile-based precursor fiber for carbon fiber, carbon fiber bundles, process for producing stabilized fiber bundles, and process for producing carbon fiber bundles
Provided are: a polyacrylonitrile-based precursor fiber for the production of a carbon fiber having a large single-fiber fineness, said precursor fiber ensuring high heat stability of a spinning dope and excellent productivity; and a copolymer suitable for the production of said precursor fiber. Also provided are: high-quality carbon fiber bundles which have a large single-fiber fineness and excellent productivity; a process for producing the same; and a process for producing flameproofed fiber bundles suitable for the production of the carbon fiber bundles. A polyacrylonitrile-based copolymer which comprises 93.0 to 99.4 mol % of acrylonitrile units, 0.5 to 4.0 mol % of (meth)acrylamide-based units, and 0.1 to 3.0 mol % of unsaturated carboxylic acid hydroxyalkyl ester units and in which the (meth)acrylamide-based units are (meth)acrylamide units and/or (meth)acrylamide derivative units having a molecular weight of 105 or less; a precursor fiber comprising the copolymer; a process for producing flameproofed fiber bundles which uses precursor fiber bundles consisting of the precursor fiber; carbon fiber bundles; and a process for production thereof.
1. A carbon fiber bundle having a maximum diameter of a single fiber of from 8 μm to 20 μm, said carbon fiber bundle obtained by calcining a precursor fiber bundle comprising a polyacrylonitrile-based precursor fiber, provided that a maximum diameter of a single fiber means the maximum value among distances between any two points on an outer circumference of a cross-section that is perpendicular to the fiber axis of the single fiber when the cross-section is observed by scanning electron microscopy (SEM),
wherein the polyacrylonitrile-based precursor fiber comprises a polyacrylonitrile-based copolymer which comprises:
an acrylonitrile unit in an amount of from 93.0 mol % to 99.4 mol %;
a (meth)acrylamide-based unit in an amount of from 0.5 mol % to 4.0 mol %; and
a hydroxyalkyl unsaturated carboxylate unit in an amount of from 0.1 mol % to 3.0 mol %,
wherein the (meth)acrylamide-based unit is one or both of a (meth)acrylamide unit and a (meth)acrylamide derivative unit having a molecular weight of 105 or less,
wherein a single fiber fineness of the polyacrylonitrile-based precursor fiber is from 1.5 dtex to 3.0 dtex, and
wherein the carbon fiber bundle has a strand tensile strength of 3800 MPa or more and a strand tensile modulus of 230 GPa or more.
2. The carbon fiber bundle of claim 1 , wherein the polyacrylonitrile-based copolymer comprises:
the acrylonitrile unit in an amount of from 93.0 mol % to 98.7 mol %;
the (meth)acrylamide-based unit in an amount of from 1.0 mol % to 4.0 mol %; and
the hydroxyalkyl unsaturated carboxylate unit in an amount of from 0.3 mol % to 3.0 mol %.
3. The carbon fiber bundle of claim 2 , wherein the polyacrylonitrile-based copolymer comprises:
the acrylonitrile unit in an amount of from 95.0 mol % to 98.7 mol %;
the (meth)acrylamide-based unit in an amount of from 1.0 mol % to 2.0 mol %; and
the hydroxyalkyl unsaturated carboxylate unit in an amount of from 0.5 mol % to 1.5 mol %.
4. The carbon fiber bundle of claim 2 , wherein the hydroxyalkyl unsaturated carboxylate unit is any one or both of a hydroxyalkyl methacrylate unit and a hydroxyalkyl acrylate unit.
5. The carbon fiber bundle of claim 3 , wherein the hydroxyalkyl unsaturated carboxylate unit is any one or both of a hydroxyalkyl methacrylate unit and a hydroxyalkyl acrylate unit.
6. The carbon fiber bundle of claim 1 , wherein the hydroxyalkyl unsaturated carboxylate unit is any one or both of a hydroxyalkyl methacrylate unit and a hydroxyalkyl acrylate unit.
7. A carbon fiber bundle having a maximum diameter of a single fiber of from 8 μm to 20 μm, said carbon fiber bundle obtained by calcining a precursor fiber bundle comprising a polyacrylonitrile-based precursor fiber, provided that a maximum diameter of a single fiber means the maximum value among distances between any two points on an outer circumference of a cross-section that is perpendicular to the fiber axis of the single fiber when the cross-section is observed by scanning electron microscopy (SEM),
wherein the polyacrylonitrile-based precursor fiber comprises a polyacrylonitrile-based copolymer which comprises:
an acrylonitrile unit in an amount of from 95.0 mol % to 98.7 mol %;
a (meth)acrylamide-based unit in an amount of from 1.0 mol % to 2.0 mol %; and
a hydroxyalkyl unsaturated carboxylate unit in an amount of from 0.5 mol % to 1.5 mol %,
wherein the (meth)acrylamide-based unit is one or both of a (meth)acrylamide unit and a (meth)acrylamide derivative unit having a molecular weight of 105 or less,
wherein the hydroxyalkyl unsaturated carboxylate unit is any one or both of a hydroxyalkyl methacrylate unit and a hydroxyalkyl acrylate unit, and
wherein the carbon fiber bundle has a strand tensile strength of 3800 MPa or more and a strand tensile modulus of 230 GPa or more.
8. A method for producing the carbon fiber bundle of claim 1 , the method comprising:
heating the precursor fiber bundle comprising the polyacrylonitrile-based precursor fiber, at a temperature of from 220° C. to 300° C. for a time of 90 minutes or less in an oxidizing atmosphere, and thereby obtaining a stabilized fiber bundle having a fiber density of from 1.35 g/cm 3 to 1.43 g/cm 3 ; and
heating the stabilized fiber bundle at a temperature of from 800° C. to 2000° C. in an inert gas, and thereby obtaining the carbon fiber bundle.
9. A method for producing the carbon fiber bundle of claim 7 , the method comprising:
heating the precursor fiber bundle comprising the polyacrylonitrile-based precursor fiber, at a temperature of from 220° C. to 300° C. for a time of 90 minutes or less in an oxidizing atmosphere, and thereby obtaining a stabilized fiber bundle having a fiber density of from 1.35 g/cm 3 to 1.43 g/cm 3 ; and
heating the stabilized fiber bundle at a temperature of from 800° C. to 2000° C. in an inert gas, and thereby obtaining the carbon fiber bundle.