Titanium alloy
View Patent ↗A titanium alloy including by mass %, a platinum group metal: 0.01 to 0.15% and a rare earth metal: 0.001 to 0.10%, with the balance being Ti and impurities. The titanium alloy preferably includes as a partial replacement for Ti, Co: 0.05 to 1.00% by mass, and the content of the platinum group metal is preferably in the range of 0.01 to 0.05% by mass. Furthermore, it is preferred that the platinum group metal be Pd and the rare earth metal be Y. Consequently, it is possible to provide a titanium alloy having corrosion resistance comparable to or better than that of the conventional art as well as good workability while offering an economic advantage with a lower content of platinum group metal or an advantage of less likelihood of corrosion growth originating at defects such as flaws that occurred in the surface.
1. A titanium alloy consisting of, by mass %, Pd as a platinum group metal: 0.01 to 0.15% and one or more selected from the group consisting of Y, La, Ce, Pr, and Nd as a rare earth metal: 0.001 to 0.0095%, with the balance being Ti and impurities, wherein, in a multiple crevice test, the titanium alloy does not suffer corrosion attack in any crevice site under a condition of 250 g/L NaCl, pH=2 adjusted with HCL, 150° C., saturated atmosphere, retained 240 hours.
2. A titanium alloy consisting of, by mass %, Pd as a platinum group metal: 0.01 to 0.15% and one or more selected from the group consisting of Y, La, Ce, Pr, and Nd as a rare earth metal: 0.001 to 0.0095%, with the balance being Ti and impurities, wherein Co is included, as a partial replacement for Ti, in an amount of 0.05 to 1.00% by mass, wherein, in a multiple crevice test, the titanium alloy does not suffer corrosion attack in any crevice site under a condition of 250 g/L NaCl, pH=2 adjusted with HCL, 150° C., saturated atmosphere, retained 240 hours.
3. A titanium alloy consisting of, by mass %, Ru as a platinum group metal: 0.01 to 0.15% and one or more selected from the group consisting of La, Ce, Pr and Nd as a rare earth metal: 0.001 to 0.0084%, with the balance being Ti and impurities, wherein, in a multiple crevice test, the titanium alloy does not suffer corrosion attack in any crevice site under a condition of 250 g/L NaCl, pH=2 adjusted with HCl, 150° C., saturated atmosphere, retained 240 hours.
4. A titanium alloy consisting of, by mass %, Ru as a platinum group metal: 0.01 to 0.15% and one or more selected from the group consisting of La, Ce, Pr and Nd as a rare earth metal: 0.001 to 0.0084%, with the balance being Ti and impurities, wherein Co is included, as a partial replacement for Ti, in an amount of 0.05 to 1.00% by mass, wherein, in a multiple crevice test, the titanium alloy does not suffer corrosion attack in any crevice site under a condition of 250 g/L NaCl, pH=2 adjusted with HCl, 150° C., saturated atmosphere, retained 240 hours.