Polyester elastomer foam
There is provided a polyester elastomer foam having a micro and uniform cell structure. The polyester elastomer foam is formed by allowing a polyester elastomer composition containing a polyester elastomer and a surface-treated inorganic substance (except hydroxides) to expand. A residue on a 166 mesh sieve in the surface-treated inorganic substance (except hydroxides) is preferably not more than 0.01%.
1. A polyester elastomer foam comprising a polyester elastomer composition containing a polyester elastomer and a surface-treated inorganic substance other than a hydroxide to expand,
wherein a residue on a 166 mesh sieve in the surface-treated inorganic substance other than a hydroxide is not more than 0.01%;
an average particle size of the surface-treated inorganic substance other than a hydroxide is 0.1 to 10 μm;
wherein the polyester elastomer foam is free of an inorganic substance having a hydroxyl group in a molecule;
the polyester elastomer foam has a semi-open/semi-closed cell structure in which a closed cell moiety occupies not more than 40% of the polyester elastomer foam;
the polyester elastomer foam has a repulsive force at 50% compression of 0.1 to 5.0 N/cm 2 , and
the polyester elastomer foam has an apparent density of 0.03 to 0.3 g/cm 3 , an average cell diameter of 10 to 150 μm, and a proportion of cells having a cell diameter of 50 to 100 μm of not less than 40% relative to all the foam cells.
2. The polyester elastomer foam according to claim 1 , wherein the surface treatment is silane coupling treatment or treatment with a higher fatty acid or a salt thereof.
3. The polyester elastomer foam according to claim 1 , wherein the inorganic substance other than a hydroxide is hard clay comprising aluminum oxide and silicon oxide or an alkaline earth metal carbonate.
4. The polyester elastomer foam according to claim 1 , wherein the polyester elastomer composition contains the surface-treated inorganic substance other than a hydroxide in an amount of 0.1 to 20% by weight relative to the total amount (100% by weight) of the polyester elastomer composition.
5. The polyester elastomer foam according to claim 1 , wherein the polyester elastomer foam is formed through the steps of impregnating the polyester elastomer composition with a high-pressure gas and then subjecting the impregnated polyester elastomer composition to decompression.
6. The polyester elastomer foam according to claim 5 , wherein the gas is an inert gas.
7. The polyester elastomer foam according to claim 6 , wherein the inert gas is carbon dioxide.
8. The polyester elastomer foam according to claim 7 , wherein the inert gas is in a supercritical state.
9. A foam material comprising a polyester elastomer foam according to claim 1 .
10. The foam material according to claim 9 , wherein the foam material has a pressure-sensitive adhesive layer on the polyester elastomer foam.
11. The foam material according to claim 10 , wherein the pressure-sensitive adhesive layer is an acrylic pressure-sensitive adhesive layer.
12. A process for producing a polyester elastomer foam, the process comprising the step of kneading a polyester elastomer composition containing a polyester elastomer and a surface-treated inorganic substance other than a hydroxide and a step of impregnating the polyester elastomer composition with a high-pressure gas to expand the polyester elastomer composition,
wherein a residue on a 166 mesh sieve in the surface-treated inorganic substance other than a hydroxide is not more than 0.01%;
an average particle size of the surface-treated inorganic substance other than a hydroxide is 0.1 to 10 μm;
wherein the polyester elastomer foam is free of an inorganic substance having a hydroxyl group in a molecule;
the polyester elastomer foam has a semi-open/semi-closed cell structure in which a closed cell moiety occupies not more than 40% of the polyester elastomer foam;
the polyester elastomer foam has a repulsive force at 50% compression of 0.1 to 5.0 N/cm 2 , and
the polyester elastomer foam has an apparent density of 0.03 to 0.3 g/cm 3 , an average cell diameter of 10 to 150 μm, and a proportion of cells having a cell diameter of 50 to 100 μm of not less than 40% relative to all the foam cells.