View Patent ↗The present invention provides a spring steel, which is finally formed into a spring, by making use of, at a maximum, the temper softening resistance effect due to alloying elements while suppressing the formation of hard inclusions of SiO 2 and the generation of decarburization, which may cause deterioration of fatigue characteristics of the spring. The spring steel is characterized by comprising, in % by mass, C: 0.50 to 0.70%, Si: 1.00 to 5.00%, Mn: 0.30 to 2.00%, P: 0.0002 to 0.0500%, S: 0.0002 to 0.0500%, Cr: 0.10 to 3.50%, Al: 0.0005 to 0.0500%, and N: 0.0020 to 0.0100%, with the balance being Fe and inevitable impurities, wherein the H-value defined by the following equation (a) is 160 or more, and the C-value defined by the following equation (b) is 3.25 or less: H=33.6[C]+10.0[Si]+5.95[Mn]+11.1[Cr]+90.0 (a), and C=[Si]/[Mn] (b).
1. A spring steel consisting of, in % by mass:
C: 0.50 to 0.70%,
Si: 3.01 to 5.00%,
Mn: 0.30 to 2.00%,
P: 0.0002 to 0.0500%,
S: 0.0002 to 0.0500%,
Cr: 0.10 to 3.50%,
Al: 0.0005 to 0.0500%, and
N: 0.0020 to 0.0100%,
with the balance being Fe and inevitable impurities,
wherein H defined by the following equation (a) is 175 or more, and C′ defined by the following equation (b) is 3.25 or less:
H=33.6[C]+10.0[Si]+5.95[Mn]+11.1[Cr]+90.0 (a),
and
C′=[Si]/[Mn] (b),
where [C], [Si], [Mn], and [Cr] represent the content (% by mass) of each element in the steel.
2. A spring produced by subjecting a steel material to a heat treatment after wire drawing, wherein the steel material consists of, in % by mass:
C: 0.50 to 0.70%,
Si: 3.01 to 5.00%,
Mn: 0.30 to 2.00%,
P: 0.0002 to 0.0500%,
S: 0.0002 to 0.0500%,
Cr: 0.10 to 3.50%,
Al: 0.0005 to 0.0500%, and
N: 0.0020 to 0.0100%,
with the balance being Fe and inevitable impurities,
wherein the spring is a spring having H defined by the following equation (a) of 175 or more, and C′ defined by the following equation (b) of 3.25 or less:
H=33.6[C]+10.0[Si]+5.95[Mn]+11.1[Cr]+90.0 (a),
and
C′=[Si]/[Mn] (b),
where [C], [Si], [Mn], and [Cr] represent the content (% by mass) of each element in the steel.
3. A spring steel consisting of, in % by mass:
C: 0.50 to 0.70%,
Si: 3.01 to 5.00%,
Mn: 0.30 to 2.00%,
P: 0.0002 to 0.0500%,
S: 0.0002 to 0.0500%,
Cr: 0.10 to 3.50%,
Al: 0.0005 to 0.0500%,
N: 0.0020 to 0.0100%, and one or more of:
Mo: 0.01 to 1.00%,
V: 0.01 to 0.30%,
Nb: 0.001 to 0.200%,
Ca: 0.0002 to 0.0100%,
Mg: 0.0002 to 0.0100%, and
Zr: 0.0005 to 0.1000%,
with the balance being Fe and inevitable impurities,
wherein H′ defined by the following equation (c) is 178 or more, and C′ defined by the following equation (b) is 3.25 or less:
H′=33.6[C]+10.0[Si]+5.95[Mn]+11.1[Cr]+21.9[Mo]+34.0[V]+90.0 (c),
and
C′=[Si]/[Mn] (b),
where [C], [Si], [Mn], [Cr], [Mo], and [V] represent the content (% by mass) of each element in the steel.
4. A spring produced by subjecting a steel material to a heat treatment after wire drawing, wherein the steel material consists of, in % by mass:
C: 0.50 to 0.70%,
Si: 3.01 to 5.00%,
Mn: 0.30 to 2.00%,
P: 0.0002 to 0.0500%,
S: 0.0002 to 0.0500%,
Cr: 0.10 to 3.50%,
Al: 0.0005 to 0.0500%,
N: 0.0020 to 0.0100%, and one or more of:
Mo: 0.01 to 1.00%,
V: 0.01 to 0.30%,
Nb: 0.001 to 0.200%,
Ca: 0.0002 to 0.0100%,
Mg: 0.0002 to 0.0100%, and
Zr: 0.0005 to 0.1000%,
with the balance being Fe and inevitable impurities,
wherein the spring is a spring having H′ defined by the following equation (c) of 178 or more, and C′ defined by the following equation (b) of 3.25 or less:
H′=33.6[C]+10.0[Si]+5.95[Mn]+11.1[Cr]+21.9[Mo]+34.0[V]+90.0 (c),
and
C′=[Si]/[Mn] (b),
where [C], [Si], [Mn], [Cr], [Mo], and [V] represent the content (% by mass) of each element in the steel.