Forming body for sealing an object to be welded, more particularly a pipe
View Patent ↗In some embodiments, a forming body for the temporary sealing of a flow cross-section of an assigned object to be welded is disclosed. In some embodiments, the forming body comprises a dimensionally stable, preferably biologically-degradable material, which has a water solubility ≧90% and of which the main component is corn starch and/or corn semolina and/or corn flakes.
1. A method for welding a steel pipe comprising:
introducing a forming body into an inner space of a steel pipe to be welded, wherein the forming body sealingly acts as a gas barrier for the temporary internal sealing of a flow cross section of the steel pipe,
welding the steel pipe under protective gas, wherein the steel pipe is sealed by the forming body during welding;
after welding, introducing a liquid into contact with the inner space of the steel pipe; and
dissolving the forming body as a result of contact with the liquid,
wherein the forming body is composed of a biologically degradable material the main constituent of which is corn starch and/or corn semolina and/or corn flakes and which has a water solubility of ≧90% and which yields an ash content of 0.29% during incineration according to DIN 51719 and a pH value of 6.6 when dissolved in fully demineralized water,
wherein the forming body, already in its initial state as produced, has a cylindrical shape and size that is adapted to the inner space of the steel pipe to ensure a reliable sealing of the inner space of the steel pipe during welding and has an edge region with a chamfer which is formed in the transitional region between an end face and a longitudinal side face of the forming body and wherein the forming body is dimensionally stable, pressure-stable, and temperature-stable so that its shape does not change when pressure and an increased temperature during welding are applied, and
when the forming body is introduced into the inner space of the steel pipe and is positioned at the desired location inside the steel pipe by means of an elongated, cylindrical introduction tool which presses onto an end face of the forming body when the forming body is pressed into the inner space of the steel pipe by means of the introduction tool, wherein the forming body is in contact with its outer circumferential face extensively against an inner circumferential face of the steel pipe.
2. The method of claim 1 , wherein the steel pipe is in a membrane wall of a steam boiler of a power plant.