High-performance high-nitrogen duplex stainless steels excellent in pitting corrosion resistance
View Patent ↗The present invention relates to high-nitrogen duplex stainless steels with an excellent eco-index and pitting corrosion resistance, in particular, to providing duplex stainless steels with ferrite-austenite phases, including: 16.5-19.5 wt. % of chromium (Cr), 2.3-3.5 wt. % of molybdenum (Mo), 1.0-5.5 wt. % of tungsten (W), 5.5-7.0 wt. % of manganese (Mn), 0.35-0.45 wt. % of nitrogen (N), with a remainder of iron (Fe). The high nitrogen duplex stainless steels with excellent eco-index and pitting corrosion resistance according to the present invention use manganese (Mn) and nitrogen (N) to exclude or mostly substitute Ni, which increases price instability of the steel grades and environment burden, to result in enhancing economic efficiency, price stability and eco-friendliness.
1. Duplex stainless steels with ferrite-austenite phases, comprising 16.5-19.5 wt. % of chromium (Cr), 2.5-3.5 wt. % of molybdenum (Mo), 2.1-5.5 wt. % of tungsten (W), 5.5-7.0 wt. % of manganese (Mn), 0.35-0.45 wt. % of nitrogen (N), 0.01 to 0.7 wt. % of nickel (Ni), with a remainder of iron (Fe) and unavoidable impurities including 0.03 wt. % or less of carbon (C) and 0.5 wt. % or less of silicon (Si).
2. The duplex stainless steels as set forth in claim 1 , having 40 to 60% volume fraction of ferrite phase.
3. The duplex stainless steels as set forth in claim 1 , having tensile strength of 820 MPa or above, and elongation of 25% or above, and wherein a product of multiplying the tensile strength by the elongation is 24000 MPa•% or above.
4. Duplex stainless steels with ferrite-austenite phases, comprising 16.5-19.5 wt. % of chromium (Cr), 2.5-3.5 wt. % of molybdenum (Mo), 2.1-5.5 wt. % of tungsten (W), 5.5-7.0 wt. % of manganese (Mn), 0.35-0.45 wt. % of nitrogen (N), excluding nickel (Ni), with a remainder of iron (Fe) and unavoidable impurities including 0.03 wt. % or less of carbon (C) and 0.5 wt. % or less of silicon (Si).
5. The duplex stainless steels as set forth in claim 4 , having 40 to 60% volume fraction of ferrite phase.
6. The duplex stainless steels as set forth in claim 4 , having tensile strength of 820 MPa or above, and elongation of 25% or above, and wherein a product of multiplying the tensile strength by the elongation is 24000 MPa•% or above.
7. Duplex stainless steels with ferrite-austenite phases, consisting of 16.5-19.5 wt. % of chromium (Cr), 2.5-3.5 wt. % of molybdenum (Mo), 2.1-5.5 wt. % of tungsten (W), 5.5-7.0 wt. % of manganese (Mn), 0.35-0.45 wt. % of nitrogen (N), with a remainder of iron (Fe) and unavoidable impurities including 0.03 wt. % or less of carbon (C) and 0.5 wt. % or less of silicon (Si).
8. The duplex stainless steels as set forth in claim 7 , having 40 to 60% volume fraction of ferrite phase.
9. The duplex stainless steels as set forth in claim 7 , having tensile strength of 820 MPa or above, and elongation of 25% or above, and wherein a product of multiplying the tensile strength by the elongation is 24000 MPa•% or above.