Water-treatment separating membrane of high flux having good chlorine resistance and method of manufacturing the same

1. A method of manufacturing a water-treatment separating membrane, the method comprising:

forming an aqueous amine solution layer on a porous support; and

forming a polyamide active layer by dropping a droplet of an organic solution comprising an acyl halide compound on the aqueous amine solution layer,

wherein a volume of the organic solution per droplet is from 0.001 ml to 5 ml,

wherein at least one curve pattern formed by connecting two or more arcs in at least a partial area of the polyamide active layer is revealed when the polyamide active layer is dyed using a 0.5% aqueous solution of Rhodamine B for showing the curve pattern, and

wherein an arithmetic mean roughness (Ra) of a surface of the polyamide active layer is from 60 nm to 100 nm.

2. The method of manufacturing a water-treatment separating membrane of claim 1 , wherein the dropping is performed by using a dropping pipette, a syringe or a spray nozzle.

3. The method of manufacturing a water-treatment separating membrane of claim 1 , wherein a dropping amount of the organic solution per a unit area of 1 m 2 is from 50 ml to 500 ml.

4. The method of manufacturing a water-treatment separating membrane of claim 1 , wherein a dropping distance of the droplet of the organic solution is regular or irregular.

5. The method of manufacturing a water-treatment separating membrane of claim 1 , wherein a dropping distance (D) of the droplet of the organic solution is from 1 mm to 50 mm.

6. The method of manufacturing a water-treatment separating membrane of claim 1 , wherein the droplets of the organic solution are dropped simultaneously or one by one.

7. The method of manufacturing a water-treatment separating membrane of claim 1 , wherein the droplets of the organic solution are dropped simultaneously in a first direction, and dropped one by one in a second direction that is perpendicular to the first direction.

8. The method of manufacturing a water-treatment separating membrane of claim 1 , wherein the forming of the polyamide active layer is performed by dropping the droplets of the organic solution including an acyl halide compound with a constant time interval on the aqueous amine solution layer while moving the porous support.

9. The method of manufacturing a water-treatment separating membrane of claim 8 , wherein the forming of the polyamide active layer is performed so as to satisfy following Equation 1:

0.25 R≦v×Δt≦ 0.75 R   Equation 1:

where v is a moving velocity of the porous support, Δt is a dropping period of the droplet of the organic solution dropped in a moving direction of the porous support, and R is a major diameter of a bottom surface of the droplet of the organic solution after completing a planarization of the droplets.

10. The method of manufacturing a water-treatment separating membrane of claim 9 , wherein the Δt is from 1/60 seconds to 1.5 seconds.

11. The method of manufacturing a water-treatment separating membrane of claim 8 , wherein the forming of the polyamide active layer comprises:

dropping the droplets of the organic solution with a constant time interval in a moving direction (MD direction) of the porous support, and

dropping the droplets of the organic solution simultaneously in a width direction (TD direction) of the porous support.

12. The method of manufacturing a water-treatment separating membrane of claim 11 , wherein a dropping distance (D) of the droplets of the organic solution dropped in the TD direction of the porous support satisfies following Equation 2:

R′≦D≦ 3/16( R 2 h )  Equation 2:

where R′ is a major diameter of a droplet just before reaching the aqueous amine solution layer, D is a dropping distance of the droplets dropped in the TD direction, R is a major diameter of a droplet of an organic solution after completing a planarization of the droplets, and h is a height of a droplet of an organic solution after completing planarization.

13. The method of manufacturing a water-treatment separating membrane of claim 8 , wherein the forming of the polyamide active layer comprises:

dropping the droplets of the organic solution at an interval in a moving direction (MD direction) of the porous support and a width direction (TD direction) of the porous support,

wherein a dropping period of the droplets of the organic solution dropped in the TD direction of the porous support is shorter than a dropping period of the droplets of the organic solution dropped in the MD direction of the porous support.

14. The method of manufacturing a water-treatment separating membrane of claim 13 , wherein the dropping period of the droplets of the organic solution dropped in the TD direction of the porous support is from 0.5 times to 0.8 times of the dropping period of the droplets of the organic solution dropped in the MD direction of the porous support.

15. A water-treatment separating membrane comprising a polyamide active layer on a porous support,

wherein the polyamide active layer is formed by dropping droplets of an organic solution comprising an acyl halide compound on an aqueous amine solution layer and includes a center portion in which a degree of an interface polymerization of the organic solution is high and a critical area in which the degree of the interface polymerization of the organic solution is low,

a volume of the organic solution per droplet is from 0.001 ml to 5 ml,

at least one curve pattern formed by connecting two or more arcs in at least a partial area of the polyamide active layer is revealed when the polyamide active layer is dyed using a 0.5% aqueous solution of Rhodamine B for showing the curve pattern, and

an arithmetic mean roughness (Ra) of a surface of the polyamide active layer is from 60 nm to 100 nm.

16. A water-treatment module comprising at least one water-treatment separating membrane of claim 15 .

17. A water-treatment apparatus comprising at least one water-treatment module of claim 16 .