Sorbent for Lithium Extraction
This invention relates to a method for preparing a lithium aluminate intercalate (LAI) matrix solid and methods for the selective extraction and recovery of lithium from lithium containing solutions, including brines. The method for preparing the LAI matrix solid includes reacting aluminum hydroxide and a lithium salt for form the lithium aluminate intercalate, which can then be mixed with up to about 25% by weight of a polymer to form the LAI matrix.
1 . A method for preparing a composition for the recovery of lithium from a brine, wherein the method comprises the steps of:
preparing a lithium aluminate intercalate solid by contacting a lithium salt with alumina under conditions sufficient to infuse the alumina with lithium salt, wherein the mole ratio of lithium to alumina is up to about 0.5:1; and
mixing the lithium aluminate intercalate solid with a polymer material in an aqueous medium to form a matrix, wherein said lithium aluminate intercalate solid is present in an amount of at least about 75% by weight and said polymer is present in an amount of between about 1% and 25% by weight, and wherein the said polymer is not an ion-exchange resin.
2 . The method of claim 1 , wherein the said polymer is selected from a group consisting of polyethylene, ultra high molecular weight polyethylene, high density polyethylene, polypropylene, poly vinyl alcohol, poly acrylic acid, polyvinylidinedifluoride, polytetrafluoroethylene, and combinations thereof.
3 . The method of claim 1 , wherein the lithium aluminate intercalate solid is present in the matrix in an amount of at least about 80% by weight and said polymer is present in an amount of between about 1% and 20% by weight.
4 . The method of claim 1 , wherein the lithium salt is lithium chloride.
5 . The method of claim 1 , wherein the alumina is selected from gibbsite, alumina hydrate, bayerite, nordstandite, bauxite, amorphous aluminum trihydroxide, and activated alumina.
6 . The method of claim 1 , wherein the matrix is sintered to form a solid.
7 . The method of claim 6 , wherein sintering the matrix comprises subjecting the matrix to pressure of at least 5000 psi and heating the matrix to a temperature of at least about 200° C.
8 . A composition for the recovery of lithium from a brine comprising particulate material containing a lithium aluminate intercalate and a polymer,
wherein the lithium aluminate intercalate is produced by infusing alumina with a lithium salt to produce a LiX/AI(OH) 3 solid having a mole fraction of lithium to aluminum of up to about 0.33, wherein X is the anion of the lithium salt,
wherein the lithium aluminate intercalate is present in an amount of at least about 75% by weight and the polymer is present in an amount of between about 1% and 25% by weight, and
and wherein the said polymer is not an ion-exchange resin.
9 . The method of claim 8 , wherein the lithium aluminate intercalate solid is present in an amount of at least about 80% by weight and said polymer is present in an amount of between about 1% and 20% by weight.
10 . The composition of claim 8 , wherein the lithium salt is lithium chloride.
11 . The composition of claim 8 , wherein the polymer is selected from the group consisting of polyethylene, ultra high molecular weight polyethylene, high density polyethylene, polypropylene, poly vinyl alcohol, poly acrylic acid, polyvinylidinedifluoride, polytetrafluoroethylene, and combinations thereof.
12 . The composition of claim 8 , wherein the polymer comprises an emulsified water insoluble polymer.
13 . The composition of claim 12 , wherein the water insoluble polymer comprises a fluoropolymer.
14 . The composition of claim 12 , wherein the water insoluble polymer is an acrylic interpolymer.
15 . The composition of claim 8 , wherein the particulate material has an average diameter of between about 100 and 450 μm.
16 . The composition of claim 8 , wherein the particulate material has an average diameter of between about 180 and 300 μm.
17 . A composition for the recovery of lithium from a brine comprising particulate material comprising a lithium alumina intercalate and a polymer,
wherein the lithium alumina intercalate is produced by infusing alumina with a lithium salt to produce a LiX/AI(OH) 3 solid having a mole fraction of lithium to aluminum of up to about 0.33, wherein X is the anion of the lithium salt,
wherein the lithium alumina intercalate is present in an amount of at least about 75% by weight and the polymer is present in an amount of between about 1% and 25% by weight, and
and wherein the polymer is selected from the group consisting of polyethylene, ultra high molecular weight polyethylene, high density polyethylene, polypropylene, poly vinyl alcohol, poly acrylic acid, polyvinylidinedifluoride, polytetrafluoroethylene, and combinations thereof.
18 . The composition of claim 17 , wherein the lithium salt is lithium chloride.
19 . The composition of claim 17 , wherein the particulate material has an average diameter of between about 100 and 450 μm.
20 . The composition of claim 17 , wherein the particulate material has an average diameter of between about 180 and 300 μm.