Advanced graphite additive for enhanced cycle-life of lead-acid batteries
An Advanced Graphite, with a lower degree of ordered carbon domains and a surface area greater than ten times that of typical battery grade graphites, is used in negative active material (NAM) of valve-regulated lead-acid (VRLA) type Spiral wound 6V/25 Ah lead-acid batteries. A significant and unexpected cycle life was achieved for the Advanced Graphite mix, where the battery was able to cycle beyond 145,000 cycles above the failure voltage of 9V, in a non-stop, power-assist, cycle-life test. Batteries with Advanced Graphite also showed increased charge acceptance power and discharge power compared to control groups.
1. An energy storage device, comprising:
an electrode comprising lead;
an electrode comprising lead dioxide;
a separator between the electrode comprising lead and the electrode comprising lead dioxide;
an aqueous solution electrolyte containing sulfuric acid; and
a carbon-based additive comprising graphite having a specific surface area of approximately 100 to 900 m 2 /g, wherein the carbon-based additive is a disordered carbon additive in negative active material with (i) crystallinity of 60% or lower, (ii) degradation onset temperature of 650° C. or lower; and (iii) degradation temperature range of a minimum 170° C. or higher, and further wherein the carbon-based additive has (i) between about 20 and 40 percent microporous carbon particles of the total amount of carbon-based additive by weight; (ii) between about 60 and 70 percent mesoporous carbon particles of the total amount of carbon-based additive by weight; and (iii) between about 0 and 10 percent macroporous carbon particles of the total amount of carbon-based additive by weight.
2. The energy storage device of claim 1 , wherein the carbon-based additive has a specific surface area of substantially 100 to 550 m 2 /g.
3. The energy storage device of claim 1 , wherein the carbon-based additive has a specific surface area of substantially 100 to 350 m 2 /g.
4. The energy storage device of claim 1 , wherein the carbon-based additive has a specific surface area of substantially 100 to 250 m 2 /g.
5. The energy storage device of claim 1 , wherein the carbon-based additive is mixed with a negative, dry, unformed paste having a surface area greater than 3 m 2 /g.
6. The energy storage device of claim 4 , wherein the concentration of the carbon-based additive relative to the paste is approximately 0.3 to 6% by weight.
7. The energy storage device of claim 4 , wherein the concentration of the carbon-based additive relative to the paste is approximately 0.3 to 3% by weight.
8. The energy storage device of claim 4 , wherein the concentration of the carbon-based additive relative to the paste is approximately 0.3 to 2% by weight.
9. The energy storage device of claim 1 , wherein the carbon-based additive is used in a paste for a negative plate of battery and has a total pore volume of greater than about 0.2 cm 3 /g with a predominant pore size of less than 20 Å.
10. The energy storage device of claim 1 wherein the carbon-based additive is used in a paste for a negative plate of battery and has a total pore volume of greater than about 0.2 cm 3 /g with a predominant pore size of 20 Å-500 Å.