Zinc-coated steel for press hardening applications and method of production
A zinc-coated steel may be produced by performing a pre-alloying heat treatment after galvannealing the steel and prior to the hot stamping the steel. The pre-alloying heat treatment is conducted at a temperature between about 850° F. and about 950° F. in an open coil annealing process. The pre-alloying heat treatment allows for shorter time at the austenitization temperature to form a desired α-Fe phase in the coating by increasing the concentration of iron. This also decreases the loss of zinc, and a more adherent oxide exists after hot stamping.
1. A method of producing steel, the method comprising the steps of:
galvannealing the steel to form a coating comprising Zn—Fe—Al on the steel, wherein the step of galvannealing includes heating in a galvannealing furnace at a temperature of 900 to 1200° F.;
pre-alloying said galvannealed coating to increase the Fe content in the coating, without any additional coating step, using a pre-alloying heat treatment, the pre-alloying heat treatment is conducted at a temperature between about 850° F. and about 950° F. prior to hot stamping, wherein the steel is subject to the pre-alloying heat treatment for a treatment time, wherein the pre-alloying heat treatment is performed using an open coil annealing process with a dwell time of about 2 hours or more while the galvannealed coating is in an as-coated condition; and
determining the treatment time of the pre-alloying heat treatment such that the Fe content in the coating is between 15 wt % and 25 wt % after the pre-alloying heat treatment.
2. The method of claim 1 , wherein the coating weight is in the range of about 40 to about 90 g/m 2 per side.
3. The method of claim 1 , wherein the treatment time of the pre-alloying heat treatment is between about 2 hours and about 6 hours.
4. The method of claim 1 , wherein the pre-alloying heat treatment is conducted in a protective atmosphere.
5. The method of claim 4 , wherein the protective atmosphere comprises nitrogen.
6. The method of claim 5 , wherein the protective atmosphere comprises about 100 vol % N 2 .
7. The method of claim 5 , wherein the protective atmosphere further comprises hydrogen.
8. The method of claim 7 , wherein the protective atmosphere comprises about 95 vol % N 2 and about 5 vol H 2 .
9. The method of claim 1 further comprising hot stamping the steel after the pre-alloying heat treatment.
10. The method of claim 9 , wherein the hot stamping step comprises an austenitizing step, wherein the austenitizing step comprises heating the steel to a temperature between about 1616° F. and about 1742° F.
11. The method of claim 9 , wherein the hot stamping step comprises an austenitizing step, wherein the austenitizing step proceeds for a predetermined duration, wherein the predetermined duration comprises a time between about 2 minutes and about 10 minutes.
12. The method of claim 9 , further determining the treatment time of the pre-alloying heat treatment such that the coating comprises solid solution α-Fe with up to approximately 30 wt % Zn after hot stamping.