A razor blade having a substrate with a cutting edge being defined by a sharpened tip. The substrate has thicknesses of 1.60-1.75 micrometers and 9.25-10.00 micrometers measured at a distance of four and forty micrometers from the blade tip, respectively. A ratio of the thickness measured at four micrometers to the thickness measured at forty micrometers is between 0.165-0.185. The substrate thickness is about 2.70-3.00 micrometers at eight micrometers from the blade tip, about 4.44-5.00 micrometers at sixteen micrometers from the blade tip with a thickness ratio measured at four micrometers and eight micrometers between 0.56-0.62, and a thickness ratio measured at four micrometers and sixteen micrometers between 0.32-0.40. The blade edge shape is defined by equation w=ad n where “a” is between 0.50-0.62 and “n” is between 0.76-0.80. An included angle of less than 7° is measured at a distance of forty micrometers or greater from the blade tip. A nitrided substrate may also be provided.
1. A razor blade comprising:
a substrate with a cutting edge being defined by a sharpened tip, said substrate having a thickness of between 1.60 and 1.75 micrometers measured at a distance of four micrometers from the sharpened tip, and a thickness of between 9.25 and 10.00 micrometers measured at a distance of forty micrometers from the sharpened tip.
2. The razor blade of claim 1 , further comprising a ratio of the thickness measured at four micrometers to the thickness measured at forty micrometers between 0.165 and 0.185.
3. The razor blade of claim 1 , wherein said substrate has a thickness of between 2.70 and 3.00 micrometers measured at a distance of eight micrometers from the sharpened tip, a thickness of between 4.44 and 5.00 micrometers measured at a distance of sixteen micrometers from the sharpened tip, a ratio of the thickness measured at four micrometers to the thickness measured at eight micrometers between 0.56 and 0.62, and a ratio of the thickness measured at four micrometers to the thickness measured at sixteen micrometers between 0.32 and 0.40.
4. The razor blade of claim 1 , wherein a cross-sectional shape of the blade is defined by the equation w=ad n , where “a” is in the range of 0.50 to 0.62, and “n” is in the range of 0.76 to 0.80.
5. The razor blade of claim 1 , wherein the substrate comprises a martensitic stainless steel of between 0.35% and 0.6% C and between 13% and 14% Cr.
6. The razor blade of claim 5 wherein said substrate further comprises between 1.1% and 1.5% Mo.
7. The razor blade of claim 1 wherein the substrate is a martensitic stainless steel having a carbide density of at least 200 carbides or more per 100 square micrometers as determined by optical microscopic cross-section.
8. The razor blade of claim 1 wherein the substrate has a tip radius of in the region of 125 to 500 angstroms.
9. The razor blade of claim 8 further comprising an interlayer joined to said substrate.
10. The razor blade of claim 9 wherein said interlayer comprises niobium, chromium, platinum, titanium, or any combination or alloys thereof.
11. The razor blade of claim 10 , further comprising a coating layer joined to said interlayer.
12. The razor blade of claim 11 wherein said coating layer comprises carbon or aluminum magnesium boride.
13. The razor blade of claim 12 further comprising an overcoat layer joined to said coating layer.
14. The razor blade of claim 13 wherein said overcoat layer comprises chromium.
15. The razor blade of claim 13 further comprising an outer layer joined to said overcoat layer.
16. The razor blade of claim 15 wherein said outer layer comprises a polymer.
17. The razor blade of claim 16 wherein said outer layer comprises polytetrafluoroethylene.
18. The razor blade of claim 12 further comprising an outer layer joined to said coating layer.
19. The razor blade of claim 1 , further comprising an included angle that is less than 7 degrees.
20. The razor blade of claim 19 wherein said included angle is measured at a distance of forty micrometers or greater from the sharpened tip.
21. The razor blade of claim 19 wherein said substrate has only two facets on each side of said cutting edge.
22. The razor blade of claim 1 , further comprising a nitride region disposed at or beneath a surface of the substrate.
23. The razor blade of claim 22 wherein said nitride region is formed by plasma nitriding.
24. The razor blade of claim 23 further comprising one or more layers joined to said nitride region.