Method for modification of lithium ion battery positive electrode material
The present invention discloses a method for modification of a lithium ion battery positive electrode material. The method comprises the following steps: (1) mixing organic acid and alcohol to obtain an organic solution; (2) adding positive electrode material into the organic solution to obtain a suspension; (3) washing with alcohol solvent after centrifugal separation; (4) drying treatment; the positive electrode material is a nickel-based metal oxide positive electrode material LiNi x M 1-x O 2 , wherein 0.5≦x<1 and M is one or two selected from the group consisting of Co, Mn, Al, Cr, Mg, Cu, Ti, Mg, Zn, Zr and V. Compared with the prior art, the method of the present invention utilizes the mixed solution of alcohol and organic acid to wash the positive electrode material thereby soluble Li salt impurities on the surface of the positive electrode material are removed and pH value of the material are significantly decreased; meanwhile, low-temperature drying treatment makes the washed material to be coated with alcohol molecules which can block air molecules, thereby the binding of water molecules and the positive electrode material are avoided and pole piece gumming are prevented, obviously improving high-temperature storage performance and cycling stability of battery. Further, the mixed solution of the alcohol and the organic acid after washing can be recycled, therefore cost is low and pollution on environment is avoided.
1. A method for modification lithium ion battery positive electrode material, comprising the following steps:
(1) mixing organic acid with alcohol to obtain an organic solution;
(2) adding the lithium ion battery positive electrode material into the organic solution to obtain a suspension by mixing;
(3) washing the material with alcohol solvent after centrifugal separation of the suspension;
(4) drying the washed lithium ion battery positive electrode material to obtain the modified lithium ion battery positive electrode material;
the lithium ion battery positive electrode material is nickel-based metal oxide positive electrode materials LiNi x M 1-x O 2 , wherein 0.5≦x<1 and M is one or two selected from the group consisting of Co, Mn, Al, Cr, Mg, Cu, Ti, Zn, Zr and V.
2. The method according to claim 1 , further comprising a recycle step after the step (3), wherein the washed liquid is subjected to distillation and separation of solvent to obtain recyclable organic acid and alcohol.
3. The method according to claim 2 , wherein the distillation and separation is conducted in super gravity bed equipment.
4. The method according to claim 1 , wherein M is one or two selected from the group consisting of Co, Mn, Al, Cr, Mg and Cu.
5. The method according to claim 1 , wherein the mixing in the step (1) applies stirring mixing with a stirring mixer.
6. The method according to claim 1 , wherein the lithium ion battery positive electrode material in the step (2) is powder.
7. The method according to claim 1 , wherein the mixing in step (2) applies stirring mixing with a stirring mixer.
8. The method according to claim 5 , wherein rotation speed of the stirring mixing in the step (1) is 50-500 rpm and mixing time is 5-80 min.
9. The method according to claim 1 , wherein mass ratio of the organic acid and alcohol in the step (1) is 1-38:19.
10. The method according to claim 1 , wherein the organic acid in the step (1) is carboxylic acid.
11. The method according to claim 10 , wherein the organic acid in the step (1) is at least one selected from the group consisting of formic acid, acetic acid, propionic acid, 2-propionic acid, valeric acid, n-caproic acid, butyric acid, trichloroacetic acid, trifluoroacetic acid and 2-methyl propionic acid.
12. The method according to claim 1 , wherein the alcohol in the step (1) is C 1-6 alcohol.
13. The method according to claim 12 , wherein the alcohol in the step (1) is at least one selected from the group consisting of methanol, ethanol, isopropanol, glycerol, butanol, pentanol, n-hexanol, 2-methoxyethanol, 2-ethoxyethanol.
14. The method according to claim 7 , wherein rotation speed of the stirring mixing in the step (2) is 50-500 rpm and mixing time is 5-300 min.
15. The method according to claim 1 , wherein mass ratio of the lithium ion battery positive electrode material and the organic solution in the step (2) is 1-12:4.
16. The method according to claim 1 , wherein rotation speed of the centrifugal separation in the step (3) is 1000-10000 rpm and centrifugal time is 60 min.
17. The method according to claim 1 , wherein the alcohol solvent in the step (3) is C 1-6 alcohol.
18. The method according to claim 1 , wherein the drying in the step (4) applies drying with vacuum oven and drying temperature is 30-120° C.
19. The method according to claim 1 , wherein the step (4) further comprises screening the positive electrode material after drying.
20. The method according to claim 1 , comprising the following steps:
(1) stirring the organic acid and alcohol with mass ratio of 1-19:19 at a rotation speed of 100-400 rpm for 10-60 min to obtain an organic solution;
(2) adding the lithium ion battery positive electrode material into the organic solution, wherein mass ratio of the lithium ion battery positive electrode material and the organic solution is 1-8:4, and stirring at 100-400 rpm for 30-240 min to obtain a suspension;
(3) placing the suspension in a centrifuge, centrifuging at 3000-8000 rpm for 5-25 min, then washing the positive electrode material post centrifugation with alcohol solvent for 3 to 5 times, and transferring the washed liquid to super gravity bed equipment to be subjected to distillation and separation of solvent to obtain recyclable organic acids and alcohols;
(4) drying the washed lithium ion batteries positive electrode material under 40-90° C., obtaining the modified lithium ion battery positive electrode material after screening.