Color stable red-emitting phosphors
View Patent ↗A color stable Mn4+ doped phosphor of formula I, A x [MF y ]:Mn 4+ I wherein A is Li, Na, K, Rb, Cs, or a combination thereof; M is Si, Ge, Sn, Ti, Zr, Al, Ga, In, Sc, Hf, Y, La, Nb, Ta, Bi, Gd, or a combination thereof; x is the absolute value of the charge of the [MF y ] ion; y is 5, 6 or 7; and wherein % intensity loss of the phosphor after exposure to light flux of at least 80 w/cm 2 at a temperature of at least 50° C. for at least 21 hours is ≦4%.
1. A process for synthesizing a Mn 4+ doped phosphor, the process comprising contacting a precursor at an elevated temperature with a fluorine-containing oxidizing agent in gaseous form, wherein the precursor is selected from the group consisting of
(A) A 2 [MF 5 ]:Mn 4+ , where A is selected from Li, Na, K, Rb, Cs, and combinations thereof; and
where M is selected from Al, Ga, In, and combinations thereof;
(B) A 3 [MF 6 ]: Mn 4+ , where A is selected from Li, Na, K, Rb, Cs, and combinations thereof; and
where M is selected from Al, Ga, In, and combinations thereof;
(C) Zn 2 [MF 7 ]: Mn 4+ , where M is selected from Al, Ga, In, and combinations thereof;
(D) A[In 2 F 7 ]: Mn 4+ where A is selected from Li, Na, K, Rb, Cs, and combinations thereof;
(E) E[MF 6 ]Mn 4+ , where E is selected from Mg, Ca, Sr, Ba, Zn, and combinations thereof;
and where M is selected from Ge, Si, Sn, Ti, Zr, and combinations thereof;
(F) Ba 0.65 Zr 0.35 F 2.70 : Mn 4+ ; and
(G) A 3 [ZrF 7 ]: Mn 4+ where A is selected from Li, Na, K, Rb, Cs and combinations thereof.
2. A process according to claim 1 , wherein the elevated temperature is any temperature in a range from about 500° C. to about 600° C.