Blends of polyamide and acid anhydride-modified polyolefins for use in golf balls

1. A golf ball, comprising:

a) a core comprising a rubber composition; and

b) an inner cover layer disposed about the core, the inner cover comprising a polyamide non-ionomeric composition, the polyamide composition comprising

i) about 40 to about 98% by weight polyamide; and

ii) about 1 to about 60% by weight of an acid anhydride-modified polyolefin, wherein the acid anhydride-modified polyolefin is an ethylene-vinyl acetate copolymer; and

iii) a plasticizer; wherein the flex modulus of the polyamide composition is greater than the flex modulus of the rubber composition;

c) an outer cover layer disposed about the inner cover layer.

2. The golf ball of claim 1 , wherein the polyamide is a transparent polyamide.

3. A golf ball, comprising:

a) dual core comprising an inner and outer core layer, the inner core having an outer surface and geometric center and the outer core layer having an outer surface and inner surface; the inner core comprising a rubber composition and the outer core layer comprising a polyamide non-ionomeric composition, the polyamide composition comprising:

i) about 40 to about 98% by weight polyamide; and

ii) about 1 to about 60% by weight of an acid anhydride-modified polyolefin, wherein the acid anhydride-modified polyolefin is an ethylene-vinyl acetate copolymer and

iii) a plasticizer;

wherein the center of the inner core and surface of the outer core layer each has a hardness, and the surface hardness of the outer core layer is greater than the center hardness of the inner core, and the flex modulus of the polyamide composition is greater than the flex modulus of the rubber composition; and

b) a cover having at least one layer disposed about the core.

4. The golf ball of claim 3 , wherein the polyamide is selected from the group consisting of polyether block-amide polymers, polyamide 6; polyamide 6,6; polyamide 6,10; polyamide 6,12; polyamide 11; polyimide 12; polyamide 6,9; and polyamide 4,6, and copolymers and blends thereof.

5. The golf ball of claim 3 , wherein the polyamide is a transparent polyamide.

6. The golf ball of claim 5 , wherein the transparent polyamide has a glass transition temperature in the range of about 75° to about 95° C.

7. The golf ball of claim 5 , wherein the transparent polyamide has a transparency of at least about 85%.

8. The golf ball of claim 7 , wherein the transparent polyamide has a transparency of at least about 90%.

9. The golf ball of claim 3 , wherein the plasticizer is selected from the group consisting of N-butylbenzenesulfonamide (BBSA); N-ethylbenzenesulfonamide (EBSA); N-propylbenzenesulfonamide (PBSA); N-butyl-N-dodecylbenzenesulfonamide (BDBSA); N,N-dimethylbenzenesulfonamide (DMBSA); p-methylbenzenesulfonamide; o,p-toluene sulfonamide; p-toluene sulfonamide; 2-ethylhexyl-4-hydroxybenzoate; hexadecyl-4-hydroxybenzoate; 1-butyl-4-hydroxybenzoate; dioctyl phthalate; diisodecyl phthalate; di-(2-ethylhexyl)adipate; and tri-(2-ethylhexyl)phosphate, an alkyl or aryl fatty acid ester.

10. The golf ball of claim 3 , wherein the center hardness of the inner core is about 15 Shore D or greater and the surface hardness of the outer core is about 40 Shore D or greater, the surface hardness of the outer core layer being greater than the center hardness of the inner core.

11. The golf ball of claim 3 , wherein the cover is a single layer having a thickness of about 0.015 to about 0.090 inches and is formed from a thermoplastic or thermoset material.

12. The golf ball of claim 3 , wherein the cover comprises two or more layers and has an overall thickness of about 0.020 to about 0.160 inches and wherein each cover layer is formed from a thermoplastic or thermoset material.