METHOD OF HEAT SEALING WOVEN POLYPROPYLENE TYPE FABRICS

1 . A method of joining polypropylene woven fabrics by the following steps:

a) coating the fabrics with materials that have a melting point that is lower than the melting point of the polypropylene fabrics to be joined together;

b) heating the coating to at least the melting point of the coating; and

c) joining the heated materials with pressure light enough to allow the coating to stay in place and generally keep the woven fabrics from touching.

2 . The method in claim 1 , wherein the fabrics are not being heated up past their melting points.

3 . The method in claim 1 , wherein the fabrics are only being heated to a point below the melting point of the woven fabric but high enough to melt the coating.

4 . The method in claim 3 , wherein by using such relatively low heat, the inventive process does not damage or reduce the strength of the fabric.

5 . The method in claim 1 , wherein low pressure is applied to clamp the fabrics together to complete the seal.

6 . The method in claim 5 , wherein the pressure is under 7 psi (48 kilopascals).

7 . The method in claim 5 wherein the pressure is 2 to 7 psi (14 to 48 kilopascals).

8 . The method in claim 5 wherein the pressure is under 2 psi (14 kilopascals).

9 . The method in claim 1 , wherein by using low heat and low pressure, only the coating itself is being joined, leaving the fabric completely undamaged and unweakened.

10 . The method in claim 1 , wherein the strength of the coating adds to the overall joint strength, and resulting joint strengths, allows one to lift higher weights with less material than can be done with the current, commonly used methods of sewing fabrics together.

11 . The method in claim 1 wherein the fabrics are similar to polypropylene.

12 . The method in claim 1 wherein the fabrics are woven of a plastic material other than polypropylene.

13 . A method of joining highly oriented polypropylene woven fabrics by the following steps:

a) coating the fabrics with a coating comprising VERSIFY™ and polyethylene resins, the coating having a melting point that is at least 5 degrees lower than the melting point of the polypropylene fabrics to be joined together;

b) heating the coating to its lower melting point; and

c) joining the heated materials with sufficient pressure to allow the coating to remain in place and yet not allow the woven fabrics to make direct contact in order to achieve at least 91% joint efficiency.

14 . The method of claim 1 , wherein the coating comprises 50% to 90% of propylene-based plastomers, propylene-based elastomers, or mixtures thereof and 10% to 50% polyethylene resins and additives, having a melting point that is at least 5 degrees lower than the melting point of the polypropylene fabrics to be joined together.

15 . The method of claim 1 , wherein the coating comprises 50% to 90% of VERSIFY™ 3000 and 10% to 50% polyethylene resins, having a melting point that is at least 5 degrees lower than the melting point of the polypropylene fabrics to be joined together.

16 . The method of claim 1 , wherein the coating comprises 50% to 90% of a propylene copolymer and 10% to 50% polyethylene resins.

17 . The method in claim 1 wherein the coating has a melting point that is at least 15% lower than the melting point of the polypropylene fabrics to be joined together.

18 . A method of joining highly oriented polypropylene woven fabrics by the following steps:

a) coating the fabrics with materials comprising about 70% VERSIFY™ and about 30% polyethylene resins, having a melting point that is at least 5 degrees lower than the melting point of the polypropylene fabrics to be joined together;

b) heating the coating to its lower melting point; and

c) joining the heated materials with sufficient pressure to allow the coating to remain in place and yet not allow the woven fabrics to make direct contact in order to achieve at least 91% joint efficiency.

19 . (canceled)