Cemented carbide necking tool
A necking tool for manufacturing of metal beverage cans, the necking tool being a cemented carbide comprising in wt % of about 18 to about 63 WC, of about 21 to about 30 TiC, of about 0 to about 27 TiN, of about 0 to about 12 NbC, of about 0 to 2 Cr 3 C 2 , of about 8 to about 14 Co and of about 0 to about 6 Ni.
1. A necking tool for manufacturing of metal beverage cans, the necking tool being a cemented carbide comprising in wt % about 18 WC, about 30 TiC, about 27 TiN, about 12 NbC, from 1 Cr 3 C 2 to 2 Cr 3 C 2 and about 14 Co.
2. The necking tool of claim 1 , wherein the cemented carbide comprises in wt % 18.08 WC.
3. The necking tool of claim 1 , wherein the cemented carbide comprises in wt % 29.66 TiC.
4. The necking tool of claim 1 , wherein the cemented carbide comprises in wt % 26.46 TiN.
5. The necking tool of claim 1 , wherein the cemented carbide comprises in wt % 11.63 NbC.
6. The necking tool of claim 1 , wherein the cemented carbide comprises in wt % 14.17 Co.
7. The necking tool of claim 1 , wherein the cemented carbide has a grade with a grain size less than about 1 μm.
8. The necking tool of claim 7 , wherein the grain size is about 0.5 to 1 μm.
9. The necking tool of claim 7 , wherein the grain size is about 0.5 to 0.9 μm.
10. The necking tool of claim 1 , wherein the cemented carbide has a density of about 6.62 g/cm 3 .
11. The necking tool of claim 1 , wherein the cemented carbide has a hardness of about 1650 kg/mm 2 .
12. The necking tool of claim 1 , wherein the cemented carbide has a coefficient of thermal expansion of about 7.49 1×10 −6 /° C.
13. A necking tool for manufacturing of metal beverage cans, the necking tool being a cemented carbide comprising in wt % about 18 WC, less than about 30 TiC, less than about 27 TiN, less than about 12 NbC, 2 Cr 3 C 2 , and about 14 Co.
14. The necking tool of claim 13 , further comprising in wt % 0 of AlN.
15. The necking tool of claim 1 , further comprising in wt % 0 of AlN.
16. A necking tool for manufacturing of metal beverage cans, the necking tool being a cemented carbide comprising in wt % about 18 WC, less than about 30 TiC, less than about 27 TiN, less than about 12 NbC, about 14 Co, 1 of Cr 3 C 2 and 0 of AlN.