Ni based forged alloy, and turbine disc, turbine spacer and gas turbine each using the same
View Patent ↗The Ni based forged alloy has a composition containing, on the basis of mass percent, Al: 0.5 to 1.0%, Cr: 17 to 21%, Fe: 17 to 19%, Nb: 4.5 to 5.5%, Ti: 0.8 to 1.3%, W: 3.0 to 6.0%, B: 0.001 to 0.03%, C: 0.001 to 0.015%, and Mo: 1.0% or less, the balance being Ni and inevitable impurities. The alloy includes carbide grains of the contained elements. The carbide grains have an average grain diameter of 20 μm or less. Thus, a Ni based forged alloy is provided which is excellent in high-temperature fatigue property and has a moderate macrosegregation property.
1. A turbine disc including the Ni based forged alloy having a composition containing, on the basis of mass percent:
Al: 0.5 to 1.0%, Cr: 17 to 21%, Fe: 17 to 19%, Nb: 4.5 to 5.5%, Ti: 0.8 to 1.3%, W: 3.0 to 6.0%, B: 0.001 to 0.03%, C: 0.001 to 0.015%, and Mo: 1.0% or less, the balance being Ni and inevitable impurities,
the alloy including carbide grains of the contained elements,
wherein the carbide grains have an average grain diameter of 20 μm or less; and
the turbine disc having a mass of 0.6 ton or more.
2. A turbine spacer including the Ni based forged alloy having a composition containing, on the basis of mass percent:
Al: 0.5 to 1.0%, Cr: 17 to 21%, Fe: 17 to 19%, Nb: 4.5 to 5.5%, Ti: 0.8 to 1.3%, W: 3.0 to 6.0%, B: 0.001 to 0.03%, C: 0.001 to 0.015%, and Mo: 1.0% or less, the balance being Ni and inevitable impurities,
the alloy including carbide grains of the contained elements,
wherein the carbide grains have an average grain diameter of 20 μm or less; and
the turbine spacer having a mass of 0.25 ton or more.
3. A gas turbine including a turbine disc and/or turbine spacer including the Ni based forged alloy having a composition containing, on the basis of mass percent:
Al: 0.5 to 1.0%, Cr: 17 to 21%, Fe: 17 to 19%, Nb: 4.5 to 5.5%, Ti: 0.8 to 1.3%, W: 3.0 to 6.0%, B: 0.001 to 0.03%, C: 0.001 to 0.015%, and Mo: 1.0% or less, the balance being Ni and inevitable impurities,
the alloy including carbide grains of the contained elements,
wherein the carbide grains have an average grain diameter of 20 μm or less; and
the gas turbine giving a power of 50 MW or more.
4. The gas turbine according to claim 3 ,
wherein the turbine disc has a mass of 0.6 ton or more and/or the turbine spacer has a mass of 0.25 ton or more.