Flux composition for brazing
View Patent ↗A flux coating composition may include a composition paste including an elastomer solution mixed with a flux powder or a flux paste. When the composition is heated during a brazing operation, the composition yields no metal oxides and ≦50 ppm of carbon, ash, fumes, smoke, or other by-product contaminants. The flux may include a binder with an acrylic resin and a plurality of synthetic rubber compounds.
1. A flux coating composition comprising:
a composition paste including an elastomer solution mixed with a flux powder or a flux paste, the elastomer solution comprising:
a binder in the amount of 10-30% by weight of the flux coating composition; and
a solvent in the amount of at least 30% by weight of the flux coating composition;
the composition yields no metal oxides and ≦50 ppm of carbon, ash, fumes, smoke, or other by-product contaminants when the composition is heated in a brazing operation.
2. The flux coating composition of claim 1 , wherein the binder comprises:
an acrylic resin with 1-methoxy-2-propanol-acetate; and
a plurality of synthetic rubber compounds with at least one of butylpolybutadiene, polyisoprene, butadienestyrene, and polyisobutylene.
3. The flux coating composition of claim 1 , wherein the composition is capable of producing a flux coating composition which, after an ambient curing operation, is sufficiently hard so as to withstand handling without a post-cure baking or hardening.
4. The flux coating composition of claim 1 , wherein the flux powder or paste is at least 30% by weight of the flux coating composition.
5. The flux coating composition of claim 1 , wherein the flux coating composition does not crack, peel, fracture, chip, break, or otherwise become non-continuous when a coated brazing material is bent, curved, conformed, or otherwise deformed during normal packaging, shipping, handling, storage, or use.
6. The flux coating composition of claim 1 , wherein the composition is applied to a brazing material in a thickness of between 0.0005 and 0.035 inches with a tolerance of +/−0.001 of an inch.
7. The flux coating composition of claim 1 , wherein the composition is applied to an exterior of a brazing material having a base metal or alloy composition of at least one of the elements of copper, silver, phosphorous, nickel, zinc, tin, cadmium, and manganese.
8. The flux coating composition of claim 1 , wherein the flux coating composition is mixed to a concentration of 60% by weight solids in preparation for a coating application to a surface.
9. The flux coating composition of claim 1 , wherein the flux coating composition includes 1-3% by weight acetyl tributyl citrate plasticizer.
10. The flux coating composition of claim 1 , wherein the flux coating position includes 18-22% by weight aliphatic polycarbonate.
11. The flux coating composition of claim 1 , wherein the flux coating composition includes 38-45% by weight solvent.
12. The flux coating composition of claim 1 , wherein the flux coating composition includes 28-35% by weight brazing flux powder.
13. The flux coating composition of claim 1 , wherein the flux coating composition includes 3-5% by weight acetyl tributyl citrate plasticizer.
14. The flux coating composition of claim 1 , wherein the flux coating composition includes 25-30% by weight aliphatic polycarbonate.
15. A flux coating composition for a brazing material comprising:
a non-hygroscopic flux up to 50% by weight;
a hinder 12-30% by weight; and
a solvent at least 30% by weight.
16. The flux coating composition of claim 15 wherein the composition yields no metal oxides and ≦50 ppm of carbon, ash, fumes, smoke, or other by-product contaminants when the composition is heated in a brazing operation.
17. The flux coating composition of claim 15 wherein the composition is applied to a brazing material in a thickness of between 0.0005 and 0.035 inches with a tolerance of +/−0.001 of an inch.
18. The flux coating composition of claim 15 wherein following an ambient curing operation, the flux coating composition withstands mechanical pressure of up to 220 psi at between 20 to 25 degrees Celsius without detaching from the brazing material.
19. The flux coating composition of claim 15 wherein the binder has a tensile strength between 500 and 600 psi between 20 to 25 degrees Celsius.
20. A flux composition used for brazing, the flux composition comprising;
a flux powder or flux paste, the flux powder or flux paste being up to 50% by weight of the flux composition;
wherein the flux powder or flux paste comprises:
at least one of borates, fluorides, chlorides, and salts; and
at least one of lithium, sodium, potassium, rubidium, cesium, and
wherein the flux composition is applied to a brazing material, the brazing material formed into a circular, oval, or elliptical shape and comprising a base metal or alloy composition of at least one of the elements of aluminium, copper, gold, platinum, silver, phosphorous, nickel, zinc, tin, cadmium, and manganese; and
wherein the flux composition melts and flows at a first temperature and the brazing material melts and flows at a second temperature, the first temperature is lower than the second temperature.