Antifogging article and method for manufacturing the same, water absorbing layer forming composition, and article for transportation apparatus

1. An antifogging article having a substrate and an antifogging film on a surface of at least a part of the substrate,

wherein:

the antifogging film has (i) a water absorbing layer formed on the substrate surface and comprises a water absorbing material with a saturated water absorption amount of 50 mg/cm 3 or more and (ii) a base layer comprising a base material with a saturated water absorption amount of 10 mg/cm 3 or less between the substrate and the water absorbing layer;

the water absorbing material is a material comprising a first cured epoxy resin as a main body, obtained by reacting a water absorbing layer forming composition comprising a first polyepoxide component, a first polyaddition curing agent, a catalyst curing agent;

the first polyepoxide component contained in the water absorbing layer forming composition is constituted only of at least two polyepoxides selected from aliphatic polyepoxides with mass average molecular weights of 800 to 3000; the water absorbing layer forming composition further comprises a silane coupling agent; a content of the silane coupling agent is 5 to 40 mass % relative to 100 mass % of the total mass of the first polyepoxide component, the first polyaddition curing agent, and the catalyst curing agent and

the base material is a material whose main body is a second cured epoxy resin obtained by reacting a base layer forming composition comprising a second polyepoxide component and a second polyaddition curing agent.

2. The antifogging article according to claim 1 , wherein the water absorbing layer forming composition further comprises a filler.

3. The antifogging article according to claim 2 , wherein a content of the filler is 0.5 to 30 mass % relative to 100 mass % of the total mass of the first polyepoxide component, the first polyaddition curing agent, and the catalyst curing agent.

4. The antifogging article according to claim 2 , wherein the filler is silica particles.

5. The antifogging article according to claim 1 , wherein the first polyaddition curing agent comprises a polyamine compound having active hydrogen.

6. The antifogging article according to claim 5 , wherein an equivalent ratio of amine active hydrogen relative to epoxy groups included in an entire solid amount contained in the water absorbing layer forming composition is 0.6 to 0.8.

7. The antifogging article according to claim 1 , wherein a content of the catalyst curing agent is 1.0 to 20 mass % relative to 100 mass % of the first polyepoxide component.

8. The antifogging article according to claim 1 , wherein the catalyst curing agent comprises an imidazole compound.

9. The antifogging article according to claim 1 , wherein a film thickness of the water absorbing layer is 5 to 40 μm.

10. The antifogging article according to claim 1 , wherein a film thickness of the base layer is 2 to 8μm.

11. The antifogging article according to claim 1 , wherein the substrate comprises soda lime glass.

12. An article for transportation apparatus, comprising the antifogging article according to claim 1 .

13. A method for manufacturing the antifogging article according to claim 1 , the method comprising:

applying and reacting the base layer forming composition on the substrate surface, so as to form the base layer comprising the base material; and

applying and reacting on a surface of the base layer the water absorbing layer forming composition, so as to form the water absorbing layer comprising the water absorbing material.

14. The antifogging article according to claim 1 , wherein the silane coupling agent has an amino group.

15. The antifogging article according to claim 1 , wherein the first polyaddition curing agent is a polyoxyalkylene polyamine, wherein an equivalent ratio of amine active hydrogen of the polyoxyalkylene polyamine to the epoxy groups derived from the first polyepoxide component is 0.6 to 0.8.