Controlled release, wood preserving composition with low-volatile organic content for treatment in-service utility poles, posts, pilings, cross-ties and other wooden structures
View Patent ↗This invention discloses a wood preservative composition for the supplemental or remedial treatment of in-service poles, posts, piling, cross ties and other wooden structures. The wood preservative composition comprises a slow-release micronized copper compound in combination with a boron compound or a fluoride compound.
1. An aqueous wood preservative paste composition comprising:
a dispersion of solid particles of a substantially insoluble copper compound in an amount of about 0.001% to about 10% by weight of the paste composition;
a boron-containing compound;
an aqueous carrier; and
a thickening agent,
wherein the paste composition has a viscosity of between 125 and 425 tenths of a millimeter (tmm) as measured using a penetrometer,
wherein at least 20% of the particles of the paste composition comprise particles having particle size greater than 25 microns, and
wherein the paste composition contains no more than 36 grams volatile organic compounds (VOCs) per liter of wood preservative coating.
2. The aqueous wood preservative paste composition of claim 1 , wherein at least 30% of the particles of the paste composition comprise particles having particle size greater than 25 microns.
3. The aqueous wood preservative paste composition of claim 2 , wherein less than 20% of the particles of the paste composition comprise particles having particle size greater than 100 microns.
4. The aqueous wood preservative paste composition of claim 1 , wherein the paste composition contains no more than 30 grams VOCs per liter of wood preservative coating.
5. The aqueous wood preservative paste composition of claim 1 , wherein the paste composition contains no more than 5 grams VOCs per liter of wood preservative coating.
6. The aqueous wood preservative paste composition of claim 1 , wherein VOCs are not detectable by gas chromatography/mass spectrometry (GC/MS), according to EPA Method 8620.
7. A method for preparing the aqueous wood preservative paste composition of claim 1 , comprising the step of blending solid particles of a substantially insoluble copper compound a boron-containing compound; an aqueous carrier; and a thickening agent, to produce a paste composition with a viscosity of between 125 and 425 tenths of a millimeter (tmm) as measured using a penetrometer, wherein at least 20% of the particles of the paste composition comprise particles having particle size greater than 25 microns.
8. The method for preparing the aqueous wood preservative paste composition of claim 7 , comprising the step of maintaining the viscosity of the aqueous wood preservative paste composition at between 275 and 425 tmm.
9. A container comprising the aqueous wood preservative paste composition of claim 1 .
10. The container of claim 9 , wherein the container is a bag.
11. A method for remedial treatment of wood, comprising the step of applying the paste composition of claim 1 to a wooden structure.
12. The method of claim 11 , wherein the wooden structure is an in-service wood product.
13. The method of claim 11 , wherein the paste composition is applied onto or into the wooden structure.
14. The method of claim 12 , wherein the in-service wood product is a utility pole, a railroad tie or a wooden bridge.
15. A method of delivering a fungitoxic amount of copper ion to an interior portion of a wooden product comprising the steps of:
applying an aqueous wood preservative paste composition comprising a dispersion of solid particles of a substantially insoluble copper compound in an amount of about 0.001% to about 10% by weight of the composition; a boron-containing compound; an aqueous carrier; and a thickening agent, wherein the paste composition has a viscosity of between 125 and 425 tenths of a millimeter (tmm) as measured using a penetrometer
wherein at least 20% of the particles of the paste composition comprise particles having particle size greater than 25 microns; and
wherein applying said aqueous wood preservative composition to said wooden structure produces penetration of copper ions into an interior portion of the wooden structure to a fungicidally effective level.
16. The method of claim 15 , wherein the aqueous wood preservative paste composition contains no more than 36 grams volatile organic compounds (VOCs) per liter of wood preservative coating.
17. The method of claim 15 , wherein the wood preservative paste composition is applied by brush.