Crosslinked polyolefins for biomedical applications and method of making same
The invention relates to a polymer composition that includes a branched alkene which is cationically polymerizable as well as a glass-forming comonomer and/or a vinyl comonomer containing benzocyclobutene as the pendant group. The structure of the polymer composition can take various forms: linear random copolymer, linear block copolymer, star random copolymer, star block copolymer, and other hyperbranched polymers. The copolymer composition can undergoes crosslinking at elevated temperatures (preferably above 180° C.).
1. A method of preparing a thermoplastic copolymer comprising:
cationic polymerizing a mixture including i) at least one branched alkene monomer, ii) at least one olefin monomer having a pendant benzocyclobutene (BCB) group, and iii) at least one initiator suitable for cationic polymerization of the mixture to form the thermoplastic copolymer;
wherein the thermoplastic copolymer formed by cationic polymerization of the mixture comprises a random distribution of a plurality of constitutional units that include constitutional units corresponding to the at least one branched alkene monomer of i) and constitutional units corresponding to the at least one olefin monomer having a pendant benzocyclobutene (BCB) group of ii); and
wherein the branched alkene monomer of i) is an isoolefin selected from the group consisting of isobutylene, 2-methyl-1-butene, 2-methyl-1-pentene, 2-methyl-1-hexene, and combinations thereof.
2. A method according to claim 1 , wherein:
the isoolefin is isobutylene.
3. A method according to claim 1 , wherein:
the at least one olefin monomer having a pendant BCB group includes a monomer having the formula
wherein R is hydrogen or an alkyl group and n is 0.
4. A method according to claim 3 , wherein:
the at least one olefin monomer having a pendant BCB group includes 4-vinylbenzocyclobutene or 2-(4-benzocyclobutenyl)-propene.
5. A method according to claim 1 , wherein:
the at least one olefin monomer having a pendant BCB group includes a monomer having the formula
wherein R is alkyl group and n is an integer ranging from 0-3.
6. A method according to claim 5 , wherein:
the at least one olefin monomer having a pendant BCB group includes 2-methyl-3-(4-benzocyclobutenyl)-propene.
7. A method according to claim 1 , wherein:
the thermoplastic copolymer further includes a glass-forming monomer selected from the group consisting of styrene, indene, α-methylstyrene, p-tert-butylstyrene, p-chlorostyrene, norbornene, and combinations thereof.
8. A method according to claim 7 , wherein:
the glass-forming monomer is styrene.
9. A method according to claim 1 , wherein:
the at least one olefin monomer having a pendant BCB group is present in amount ranging from 0.01 to 60 mol % of the monomeric units of the thermoplastic polymer.
10. A method according to claim 1 , wherein:
the cationic polymerizing involves living cationic polymerization.
11. A method according to claim 1 , wherein:
the thermoplastic copolymer undergoes crosslinking when exposed to temperatures of at least 180° C.
12. A method according to claim 1 , wherein:
the at least one initiator comprises a Lewis acid initiator.
13. A method according to claim 1 , wherein:
the at least one branched alkene monomer of i) and the at least one olefin monomer having a pendant benzocyclobutene (BCB) group of ii) are added contemporaneously to the mixture during the cationic polymerizing of the mixture.
14. A method of preparing a thermoset polymer comprising:
processing a thermoplastic copolymer prepared according to claim 1 to form a resultant thermoset polymer, wherein the processing includes heating the thermoplastic copolymer such that thermoplastic copolymer undergoes crosslinking to form the resultant thermoset polymer.
15. A method of preparing an implantable medical device comprising:
processing a thermoplastic copolymer prepared according to claim 1 to form at least part of the implantable medical device, wherein the processing includes heating the thermoplastic copolymer such that the thermoplastic copolymer undergoes crosslinking to form a resultant thermoset polymer that is part of the implantable medical device.
16. A method according to claim 15 , wherein:
the implantable medical device comprises an intraocular lens.
17. A thermoset polymer comprising:
a copolymer having a random distribution of a plurality of constitutional units that include first and second constitutional units;
wherein the first constitutional units are derived from at least one cationically polymerizable branched alkene monomer, wherein the branched alkene monomer is an isoolefin selected from the group consisting of isobutylene, 2-methyl-1-butene, 2-methyl-1-pentene, 2-methyl-1-hexene, and combinations thereof;
wherein the second constitutional units are derived from at least one cationically polymerizable olefin monomer having a pendant benzocyclobutene (BCB) group; and
wherein the copolymer is crosslinked by application of heat.
18. A thermoset polymer according to claim 17 , wherein:
the isoolefin is isobutylene.
19. A thermoset polymer according to claim 17 , wherein:
the at least one olefin monomer having a pendant BCB group includes a monomer having the formula
wherein R is hydrogen or an alkyl group and n is 0.
20. A thermoset polymer according to claim 19 , wherein:
the at least one olefin monomer having a pendant BCB group includes 4-vinylbenzocyclobutene or 2-(4-benzocyclobutenyl)-propene.
21. A thermoset polymer according to claim 17 , wherein:
the at least one olefin monomer having a pendant BCB group includes a monomer having the formula
wherein R is alkyl group and n is an integer ranging from 0-3.
22. A thermoset polymer according to claim 21 , wherein:
the at least one olefin monomer having a pendant BCB group includes 2-methyl-3-(4-benzocyclobutenyl)-propene.
23. A thermoset polymer according to claim 17 , wherein:
the thermoplastic copolymer further includes a glass-forming monomer selected from the group consisting of styrene, indene, α-methylstyrene, p-tert-butylstyrene, p-chlorostyrene, norbornene, and combinations thereof.
24. A thermoset polymer according to claim 17 , wherein:
the copolymer is crosslinked by application of heat at a temperature of at least 180° C.