A phenol-free overbased alkaline earth metal carboxylate is obtained by reacting a cyclic ether alcohol, an alkaline earth metal hydroxide, a fatty carboxylic acid, carbon dioxide, an optional fatty alcohol, and an optional liquid hydrocarbon solvent or oil.
1. A plastic composition including the phenol-free overbased alkaline earth metal carboxylate made by a method comprising:
a. providing and reacting the following to form a reaction mixture:
i. cyclic ether alcohol,
ii. alkaline earth metal hydroxide, and
iii. optionally a hydrocarbon solvent or oil and
b. heating the reaction mixture to a temperature of 250-280° F.,
c. adding (iv) a fatty acid to the reaction mixture,
d. adding (v) carbon dioxide to the reaction mixture, to produce the phenol-free overbased alkaline earth metal carboxylate and water, and
e. distilling at a temperature of over 280 to 300° F. to remove residual water, wherein no phenol or compound containing a phenol group is present in the reaction mixture.
2. A halogenated polymer including the phenol-free overbased alkaline earth metal carboxylate made by a method comprising:
a. providing and reacting the following to form a reaction mixture:
i. cyclic ether alcohol,
ii. alkaline earth metal hydroxide, and
iii. optionally a hydrocarbon solvent or oil and
b. heating the reaction mixture to a temperature of 250-280° F.,
c. adding (iv) a fatty acid to the reaction mixture,
d. adding (v) carbon dioxide to the reaction mixture, to produce the phenol-free overbased alkaline earth metal carboxylate and water, and
e. distilling at a temperature of over 280 to 300° F. to remove residual water, wherein no phenol or compound containing a phenol group is present in the reaction mixture.
3. The halogenated polymer of claim 2 , wherein the halogenated polymer is selected from the group consisting of vinyl halide resin, polyvinyl chloride, copolymers of polyvinyl chloride, chlorinated polyethylene, chlorosulfonated polyethylene, chlorinated polyvinyl chloride, vinylidene chloride polymers, vinyl chloride-vinyl ester copolymers, vinyl chloride-vinyl ether copolymers, vinyl chloride-vinylidene copolymers, vinyl chloride-propylene copolymers, chlorinated polyethylene, polyvinyl bromide, polyvinyl fluoride, copolymers thereof and combinations thereof.