Polymer latex with improved mechanical properties and process for preparing said polymer latex
View Patent ↗The present invention relates to a process for preparing a polymer latex that includes polymerizing one or more ethylenically unsaturated aromatic monomers and one or more conjugated diene monomers in the presence of a hydroperoxide chain transfer agent and sulfur-containing chain transfer agent, wherein the sulfur-containing chain transfer agent is added after the hydroperoxide chain transfer agent. It further relates to the polymer latex thus obtained, to a composition comprising the polymer latex and to the use of the polymer latex or polymer latex composition in a carpet backing, paper coating, or fiber fabric pre-impregnation process.
1. A process for preparing a polymer latex comprising polymerizing one or more ethylenically unsaturated aromatic monomers and one or more conjugated diene monomers in the presence of hydroperoxide chain transfer agent and sulfur-containing chain transfer agent, wherein the sulfur-containing chain transfer agent is added after at least 80 wt % of the hydroperoxide chain transfer agent has been introduced in the process, as the polymerization proceeds, and wherein the sulfur-containing chain transfer agent is added continuously over at least 20% of the total polymerization time.
2. The process according to claim 1 , wherein the hydroperoxide chain transfer agent is an organic hydroperoxide.
3. The process according to claim 1 , wherein the sulfur-containing chain transfer agent is an alkyl mercaptan.
4. The process according to claim 1 , wherein 0.5 to 10 parts by weight of hydroperoxide chain transfer agent and 0.1 to 10 parts by weight of sulfur-containing chain transfer agent is used, based on 100 parts by weight of the total amount of monomers.
5. The process according to claim 1 , wherein
(A) 10 to 90 wt % of one or more ethylenically unsaturated aromatic monomers,
(B) 10 to 80 wt % of one or more conjugated diene monomers,
(C) 0 to 70 wt % of one or more acrylate monomers, and
(D) the remaining amount of one or more polymerizable comonomers are polymerized, with the sum of the amount of the monomers (A), (B), (C), and (D) being 100 wt %.
6. The process according to claim 5 , wherein the (A) monomers are styrene and the (B) monomers are 1,3-butadiene.
7. The process according to claim 5 , wherein the monomer (D) includes acrylonitrile.
8. The process according to claim 1 , wherein the polymerization is carried out at a temperature of from 50 to 95° C.
9. The process according to claim 1 , wherein the polymerization is an emulsion polymerization.