Chocolate product and process for producing the same
The present invention relates to a process for the manufacture of a chocolate product involving the use of hydrated salt, hydrated sugar or hydrated sugar alcohol in the underlying chocolate mass and comprising the steps of refining, conching and optionally tempering of the chocolate mass. The invention further relates to a chocolate product comprising a chocolate mass comprising certain weight proportions of hydratable salt, hydratable sugar or hydratable sugar alcohol, as obtainable by the process of the invention.
1. A process for the manufacture of a heat resistant chocolate product comprising the steps of:
(i) combining at least
(A) one or more fats selected from cocoa butter, cocoa butter alternatives, milk fat and vegetable fats which are liquid at standard ambient temperature and pressure, and
(B) one or more of hydrated salts, hydrated sugars and hydrated sugar alcohols, to form a chocolate mass having a total amount of fats of 15 to 35 wt. % and total amount of hydrated salts, hydrated sugars, and hydrated sugar alcohols of 1 to 15 wt. %;
(ii) refining the chocolate mass; and
(iii) conching the chocolate mass to a liquid;
wherein the temperature of the chocolate mass during refining and conching does not exceed 50° C., and wherein the chocolate mass comprises 1 to 15 wt. % of dextrose monohydrate as component (B) or part thereof.
2. The process according to claim 1 , wherein the temperature of the chocolate mass in the process does not exceed 40° C.
3. The process according to claim 1 , wherein refining and conching are conducted as a combined step.
4. The process according to claim 1 , wherein conching is conducted for a time not exceeding 120 minutes.
5. The process according to claim 1 , wherein the chocolate mass comprises 5 to 15 w. % of dextrose monohydrate as component (B) or part thereof.
6. The process according to claim 1 , further comprising tempering the chocolate mass at a temperature not exceeding 50° C.
7. The process according to claim 1 , wherein the chocolate product is a block molded chocolate or a chocolate coating.
8. The process according to claim 6 , further comprising, after the tempering step, a thermo-curing step at a temperature not exceeding 40° C.
9. The process according to claim 8 , wherein the thermo-curing step is carried out at a temperature in the range of from 30 to 40° C., wherein the chocolate product is load-bearing.