STABILIZED POLYCARBONATE/ACRYLONITRILE/STYRENE/ACRYLIC ESTER MOULDING COMPOUNDS
Thermoplastic molding compositions comprising the following components: a) 3 to 91.7 wt % of at least one aromatic polycarbonate, as component A b) 3 to 91.7 wt % of one or more styrene copolymers, as component B c) 3 to 91.7 wt % of one or more impact-modifying grafted rubbers without olefinic double bonding in the rubber plase, as component C, and also d) 0.2 to 0.9 wt % of a compound of formula (I), as component D: e) 0 to 0.9 wt % of a mixture of formula (II), as component E: n=2 to 20 f) 0 to 0.9 wt % of a triazine stabilizer, and also, optionally further components, with the proviso that when component E amounts to 0 wt %, at least one further stabilizer is present in an amount of 0.01 to 0.9 wt %, have good weathering properties.
1 . A thermoplastic molding composition comprising the following components:
a) 3 to 91.7 wt % of at least one aromatic polycarbonate, as component A
b) 3 to 91.7 wt % of one or more styrene copolymers, as component B
c) 3 to 91.7 wt % of one or more impact-modifying grafted rubbers without olefinic double bonding in the rubber phase, as component C
d) 0.2 to 0.9 wt % of a compound of formula (I), as component D:
e) 0 to 0.9 wt % of a mixture of formula (II), as component E:
n=2 to 20
f) 0 to 0.9 wt % of a compound of formula (III), as component F:
or 0 to 0.9 wt % of a compound of formula (IV):
where n=2 to 20
or 0 to 0.9 wt % of a compound of formula (V):
where n=2 to 20
or 0 to 0.9 wt % of a compound of formula (VI):
where n=2 to 20
g) 0 to 25 wt % of at least one halogen-free phosphorous compound G
h) 0 to 10 wt % of one or more added-substance materials other than components D, E, F and G, as component H, and
i) 0 to 40 wt % of fibrous or particulate fillers, as component I,
with the proviso that when component E amounts to 0 wt %, at least one of the components of formulae (III), (IV), (V) or (VI) is present in an amount of 0.01 to 0.9 wt %, wherein the wt % are each based on the overall weight of components A to I, and these add up to 100 wt %.
2 . The thermoplastic molding composition according to claim 1 , characterized in that the swelling index of component C is in the range from 6 to 20.
3 . The thermoplastic molding composition according to claim 1 , characterized in that component B comprises a copolymer of acrylonitrile, styrene and/or a-methylstyrene, phenylmaleimide, methyl methacrylate or mixtures thereof.
4 . The thermoplastic molding composition according to claim 1 , characterized in that component C comprises a mixture of an acrylate-styrene-acrylonitrile (ASA) graft polymer comprising 55 to 80 wt %, based on C, of an elastomer-crosslinked acrylic ester polymer C1 and 45 to 20 wt %, based on C, of a graft sheath C2 formed from a vinylaromatic monomer and one or more polar, copolymerizable, ethylenically unsaturated monomers, optionally a further copolymerizable, ethylenically unsaturated monomer in a weight ratio of from 80:20 to 65:35.
5 . The thermoplastic molding composition according to claim 1 , characterized in that in component C component C1 comprises from 0.01 to 20 wt %, preferably from 0.1 to 5 wt %, of a crosslinking monomer, preferably butylene diacrylate, divinylbenzene, butaynediol dimethacrylate, trimethylolpropane tri(meth)acrylate, diallyl methacrylate, diallyl maleate, diallyl fumarate, triallyl methacrylate, triallyl isocyanurate, more preferably diallyl phthalate, allyl methacrylate and/or dihydrodicyclopentadienyl acrylate.
6 . The thermoplastic molding composition according to claim 1 , characterized in that the average particle diameter of component C is between 50 to 1200 nm.
7 . The thermoplastic molding composition according to claim 1 , characterized in that the weight ratio of components D and E is in the range from 4:1 to 1:1 and the weight ratio of components E and F is in the range from 2:1 to 0.5:1.
8 . The thermoplastic molding composition according to claim 1 , characterized in that the molding composition can comprise from 0 to 1.5 wt % of phthalic ester or adipic ester.
9 . The thermoplastic molding composition according to claim 1 , characterized in that component C1 comprises from 2 to 99 wt % of butyl acrylate.
10 . The thermoplastic molding composition according to claim 1 , characterized in that the vinylaromatic component in C2 comprises either styrene or a-methylstyrene.
11 . The thermoplastic molding composition according to claim 1 , characterized in that the ethylenically unsaturated component in C2 comprises acrylonitrile and/or alkyl methacrylates and/or alkyl acrylates having C 1 -C 8 alkyl.
12 . The thermoplastic molding composition according to claim 1 , characterized in that component C comprises a grafted rubber in monomodal or bimodal particle size distribution.
13 . A process for producing a thermoplastic molding composition according to claim 1 , characterized in that components A to D and, optionally, components E to I are mutually mixed with one another in any desired order at temperatures of 100 to 300° C. and a pressure of 1 to 50 bar, then kneaded and extruded.
14 . The process for producing a thermoplastic molding composition according to claim 13 , characterized in that first a portion of component C is premixed with a portion of component B in a ratio of 1:1 to 1:2 to form a masterbatch and then mixed with further components A to D and optionally components E to I to form the thermoplastic molding composition.
15 . (canceled)
16 . (canceled)
17 . A molded article, a fiber or a self-supporting film or sheet comprising a thermoplastic molding composition according to claim 1 .
18 . A molded article, a fiber or a self-supporting film or sheet according to claim 17 in the form of a molded automotive component or electronic equipment part.
19 . The thermoplastic molding composition according to claim 1 , with the proviso that when component E amounts to 0 wt %, at least one of the components of formulae (Ill), (IV), (V) or (VI) is present in an amount of 0.1 to 0.9 wt %, wherein the wt % are each based on the overall weight of components A to I, and these add up to 100 wt %.
20 . The thermoplastic molding composition according to claim 1 , with the proviso that when component E amounts to 0 wt %, at least one of the components of formulae (III), (IV), (V) or (VI) is present in an amount of 0.2 to 0.8 wt %, wherein the wt % are each based on the overall weight of components A to I, and these add up to 100 wt %.