Polybutylene terephthalate resin composition and welded body
View Patent ↗To provide a polybutylene terephthalate resin composition offering excellent flowability, wherein the resin composition raises the weld strength and heat shock resistance of a welded body obtained by welding together molded products obtained by molding the polybutylene terephthalate resin composition. [Solution] A polybutylene terephthalate resin composition comprising a polybutylene terephthalate resin (A) having a weight-average molecular weight of 60,000-80,000 inclusive and an inorganic filler (B). Preferably, also included is 5-20 mass parts of an elastomer (C) relative to 100 mass parts of the polybutylene terephthalate resin (A).
1. A method of obtaining a welded body, comprising:
providing at least two molded parts, each being composed of a polybutylene terephthalate resin composition, wherein the polybutylene terephthalate resin composition consisting of a thermoplastic resin blend, and an inorganic filler, wherein the thermoplastic resin blend consists of an unmodified polybutylene terephthalate resin and optionally an elastomer, where the weight-average molecular weight of the unmodified polybutylene terephthalate resin is 60,000 or more and 80,000 or less, wherein if the optional elastomer is present in the polybutylene terephthalate resin composition, the composition contains the optional elastomer in an amount of 5 to 20 parts by mass based on 100 parts by mass of the polybutylene terephthalate resin;
placing the molded parts to abut each other at a contact surface;
moving the abutted molded parts relative to each other such that frictional heat causes the abutted molded parts to melt in the vicinity of the contact surface and causes melted polybutylene terephthalate resin composition from the abutted molded parts to flow and mix in vicinity of the contact surface; and
cooling the melted polybutylene terephthalate thereby adhering the abutted molded parts into a single body.
2. The method of claim 1 , wherein the weight-average molecular weight of the unmodified polybutylene terephthalate resin is 66,500 or more and 75,000 or less.
3. The method of claim 1 , wherein the unmodified polybutylene terephthalate resin has a crystallization temperature of 190° C. or higher.