Alloyed hot-dip galvanized steel sheet
View Patent ↗A high-strength alloyed hot-dip galvanized steel sheet obtained by subjecting the surface of a high-strength steel sheet to alloyed hot-dip galvanization, and formed from a steel sheet containing, in mass %, main components, and containing at least 40 vol % bainite and/or martensite, 8-60 vol % retained austenite, and less than 40 vol % ferrite, with the remainder comprising unavoidable structures. In the alloyed hot-dip galvanized steel sheet, the total thickness of the Gamma1 layer and the Gamma layer (Tgamma1+Tgamma) is 2 μm or less in the alloy layers formed by hot-dip galvanization, and the Gamma1 phase/Gamma phase thickness ratio (Tgamma1/Tgamma) is 1 or less. A tensile strength of 980 MPa or above can be easily imparted to the alloyed hot-dip galvanized steel sheet. The alloyed hot-dip galvanized steel sheet has excellent coating adherence, and coating separation during machining can be suppressed.
1. An alloyed hot-dip galvanized steel sheet, which is a steel sheet comprising, in mass %,
C: from 0.10 to 0.4%,
Si: from 0.01 to 0.5%,
Mn: from 1.0 to 3.0%,
O: 0.006% or less,
P: 0.04% or less,
S: 0.01% or less,
Al: from 0.1 to 3.0%, and
N: 0.01% or less, with the balance being Fe and unavoidable impurities,
wherein the structure of the steel sheet further comprises, in terms of volume fraction, 40% or more of the total content of bainite and martensite, from 8 to 60% of retained austenite, and less than 40% of ferrite, with the balance being an unavoidable structure, and alloying hot-dip galvanization is applied to the steel sheet surface;
the alloyed hot-dip galvanized layer contains a Γ1 layer;
a total thickness of the thickness Tγ1 of the Γ1 layer and the thickness Tγ of a Γ layer in the alloyed hot-dip galvanized layer is 2 μm or less and the ratio (Tγ1/Tγ) of thickness between a Γ1 phase and a Γ phase is 1 or less;
the alloyed hot-dip galvanized layer contains a ζ layer and a δ layer; and
the ratio {(Tζ+Tδ)/(Tγ1+Tγ)} of the total thickness of thickness Tζ of the ζ layer and thickness Tδ of the δ layer in the alloyed hot-dip galvanized layer to the total thickness of the Γ1 layer and the Γ layer is from 1.5 to 90.
2. The alloyed hot-dip galvanized steel sheet according to claim 1 , wherein the steel sheet further comprises one member or two or more members of, in mass %,
Cr: from 0.05 to 1.0%,
Ni: from 0.05 to 1.0%,
Cu: from 0.05 to 1.0%,
Nb: from 0.005 to 0.3%,
Ti: from 0.005 to 0.3%,
V: from 0.005 to 0.5%,
B: from 0.0001 to 0.01%,
Ca: from 0.0005 to 0.04%,
Mg: from 0.0005 to 0.04%,
La: from 0.0005 to 0.04%,
Ce: from 0.0005 to 0.04%, and
Y: from 0.0005 to 0.04%.