BENZOXAZINE RESIN COMPOSITION, AND FIBER-REINFORCED COMPOSITE MATERIAL
Provided are a fiber-reinforced composite material capable of achieving excellent CAI, ILSS, and bending fracture toughness concurrently at high levels, and maintaining a high glass transition temperature of the resin material therein, and prepreg and a benzoxazine resin composition therefor. The composition contains, at a particular ratio, (A) a compound having in its molecule a benzoxazine ring represented by formula (1), (B) an epoxy resin, (C) a curing agent, (D) a toughness improver, and (E) polyamide 12 particles of a particular particle size, and component (D) is dissolved: (R 1 : C1-C12 chain alkyl group or the like, and H is bonded to at least one of Cs of the aromatic ring at o- or p-position with respect to the carbon atom to which the oxygen atom is bonded).
1 . A benzoxazine resin composition comprising:
(A) a compound having in its molecule a benzoxazine ring represented by the formula (I):
wherein R 1 stands for a chain alkyl group having 1 to 12 carbon atoms, a cyclic alkyl group having 3 to 8 carbon atoms, a phenyl group, or a phenyl group substituted with a chain alkyl group having 1 to 12 carbon atoms or a halogen, and a hydrogen atom is bonded to at least one of the carbon atoms of the aromatic ring at ortho- or para-position with respect to the carbon atom to which the oxygen atom is bonded;
(B) an epoxy resin;
(C) a curing agent;
(D) a toughness improver; and
(E1) polyamide 12 particles having an average particle size of not smaller than 1 μm and smaller than 15 μm;
wherein a content of said component (A) is 65 to 78 mass % and a content of said component (B) is 22 to 35 mass %, with a total of components (A) and (B) being 100 mass %,
wherein, with respect to 100 parts by mass of the total of components (A) and (B), a content of said component (C) is 5 to 20 parts by mass, a content of said component (D) is 3 to 20 parts by mass, and a content of said component (E1) is 20 to 30 parts by mass, and
wherein the component (D) is dissolved.
2 . A benzoxazine resin composition comprising:
(a) a compound having in its molecule a benzoxazine ring represented by formula (1):
wherein R 1 stands for a chain alkyl group having 1 to 12 carbon atoms, a cyclic alkyl group having 3 to 8 carbon atoms, a phenyl group, or a phenyl group substituted with a chain alkyl group having 1 to 12 carbon atoms or a halogen, and a hydrogen atom is bonded to at least one of the carbon atoms of the aromatic ring at ortho- or para-position with respect to the carbon atom to which the oxygen atom is bonded;
(B) an epoxy resin;
(C) a curing agent;
(D) a toughness improver; and
(E2) polyamide 12 powder particles having an average particle size of not smaller than 15 μm and not larger than 60 μm;
wherein a content of said component (A) is 65 to 78 mass % and a content of said component (B) is 22 to 35 mass %, with a total of components (A) and (B) being 100 mass %;
wherein, with respect to 100 parts by mass of the total of components (A) and (B), a content of said component (C) is 5 to 20 parts by mass, a content of said component (D) is 3 to 20 parts by mass, and a content of said component (E2) is not less than 5 parts by mass and less than 20 parts by mass, and
wherein the component (D) is dissolved.
3 . The benzoxazine resin composition according to claim 1 , wherein said toughness improver (D) is at least one selected from the group consisting of organic fine particles and a solution of organic fine particles in a liquid resin or a resin monomer.
4 . The benzoxazine resin composition according to claim 1 , wherein said epoxy resin (B) is at least one epoxy resin selected from the group consisting of cresol novolak type epoxy resin, phenol novolak type epoxy resin, biphenyl type epoxy resin, naphthalene type epoxy resin, aromatic glycidyl ester type epoxy resins, aromatic amine type epoxy resins, resorcin type epoxy resins, and alicyclic type epoxy resins.
5 . The benzoxazine resin composition according to claim 1 , wherein said curing agent (C) is at least one selected from the group consisting of aromatic amines, monofunctional phenols, polyfunctional phenol compounds, and polyphenol compounds.
6 . A prepreg obtained by impregnating a reinforcing fiber substrate with the benzoxazine resin composition according to claim 1 .
7 . A fiber-reinforced composite material comprising a cured product of the benzoxazine resin composition according to claim 1 , and a reinforcing fiber substrate.
8 . The fiber-reinforced composite material according to claim 7 , wherein said composite material has a compression after impact strength (CAI) of not lower than 290 MPa as measured according to SACMA SRM 2R-94, an interlaminar shear strength (ILSS) of not lower than 50 MPa as measured according to ASTM D2402-07, and a bending fracture toughness of not lower than 1.2 MPa·M 1/2 as measured according to ASTM D5045, and a cured product obtained by curing said benzoxazine resin composition at 180° C. for 2 hours has a glass transition temperature of not lower than 190° C.