Process for producing high-strength hot-dip galvanized steel sheet
View Patent ↗A high-strength hot-dip galvanized steel sheet containing a main component, the steel sheet having at least 40 wt. % of ferrite as a main phase in terms of the volumetric ratio, and 8-60% inclusive of residual austenite, the remaining structure comprising one or more of bainite, martensite, or pearlite. Austenite particles within a range where the average residual stress (sigmaR) thereof satisfies the expression −400 MPa<=sigmaR<=200 MPa (formula (1)) are present in an amount of 50% or more in the hot-dip galvanized steel sheet. The surface of the steel sheet has a hot-dip galvanized layer containing less than 7 wt. % of Fe, the remainder comprising Zn, Al and inevitable impurities.
1. A process for producing a hot-dip galvanized steel sheet, comprising subjecting a steel material comprising, in mass %,
C: from 0.10 to 0.4%,
Si: from 0.01 to 0.5%,
Mn: from 1.0 to 3.0%,
O: 0.006% or less,
P: 0.04% or less,
S: 0.01% or less,
Al: from 0.1 to 3.0%,
N: 0.01% or less, and
Si+Al≧0.5%, with the balance being Fe and unavoidable impurities, to a hot rolling treatment at a hot-rolled slab temperature of 1,100° C. or more and a finishing temperature of 850 to 970° C.,
cooling the steel sheet after the hot rolling to a temperature region of 650° C. or less at 10 to 200° C./sec on average, and taking it up in a temperature range of 650° C. or less,
cold-rolling the steel sheet at a rolling reduction ratio of 40% or more,
annealing the steel sheet by setting the maximum temperature during annealing to be from 700 to 900° C., cooling the steel sheet to a temperature region of 350 to 550° C. at an average cooling rate of 0.1 to 200° C./sec, and then holding it in the temperature region for 1 to 1,000 seconds, and
immersing the steel sheet after holding in the temperature region in a hot-dip galvanizing bath and after the plating treatment, applying an alloying treatment at a temperature of 470 to 580° C.,
wherein at the time of holding the steel sheet in a temperature region of 350 to 550° C., the steel sheet is repeatedly bent using a roll having a roll diameter of 50 to 2,000 mm to thereby impart a strain to the steel sheet, and
the longitudinal average stress applied to the steel sheet during the repeated bending is from 2 to 50 MPa.
2. The process for producing a hot-dip galvanized steel sheet according to claim 1 , wherein the number of passes during the repeated bending is from 2 to 6.