Method for manufacturing a composite panel

1. A method of manufacturing a composite panel, comprising:

providing a first textile layer;

applying a first adhesive to at least a portion of the first textile layer;

forming a reinforcement fabric to the outer shape of a plurality of first profiles by folding or creasing using a forming apparatus;

placing or forming a plurality of first profiles adjacent to each other onto at least a portion of the first textile layer which has been contacted with the first adhesive,

wherein each of the first profiles comprises a foam core and the reinforcement fabric located on the foam core, and

wherein each of the first profiles is obtained by bonding a respective foam core to the pre-formed reinforcement fabric;

applying, at least once, at least one second profile between two first profiles in such a manner that a foam is provided between two first profiles, wherein the foam, when applied, is not completely cured and still possesses a residual tackiness to the reinforcement fabric such that it bonds to the reinforcement fabric with superficial contact which does not extend into the depth of the fabric;

testing the foam to determine tackiness; and

providing a second textile layer onto the at least one second profile.

2. The method according to claim 1 , wherein at least one of the first and/or the second profile are a composite profile comprising at least one each of:

a foam core with opposing frontal faces and a plurality of side faces of said foam core; and

the reinforcement fabric which is at least partially in direct contact with at least two adjacent side faces, wherein:

the reinforcement fabric is a woven textile or an at least bi-directionally oriented non-woven textile,

the foam core does not or not completely penetrate into the reinforcement fabric, and

at least on one side face of the composite profile the foam core is not permanently covered by the reinforcement.

3. The method according to claim 2 , wherein in at least one of the first and/or second profile the foam core comprises a polyurethane foam, an epoxy resin foam, a polyester resin foam, an expanded polystyrene foam and/or an expanded polypropylene foam.

4. The method according to claim 2 , wherein in at least one of the first and/or second profile the foam core comprises a polyurethane foam obtainable by reaction of a mixture comprising:

component A, wherein: component A is a polyol formulation comprising:

one or more polyether polyol(s) and/or one or more polyester polyol(s) and/or polyamines with hydroxyl number(s) from 12 to 1200 mg KOH/g, and molecular weight(s) from 60 to 7000 g/mol, and functionality from 2 to 8;

none, one or more cross linker(s) and/or chain extender(s) with hydroxyl number(s) from 500 to 2000 mg KOH/g, and molecular weight(s) from 60 to 400 g/mol, and functionality from 2 to 8;

one or more amine and/or organometallic and/or metallic catalyst(s);

none, one or more flame retardant(s) which may be halogenated;

one or more surfactants; and

one or more chemical and/or physical blowing agents; and

component B, wherein component B is an isocyanate comprising:

diphenylmethane diisocyanate and/or polymeric diphenylmethane diisocyanate optionally with a monomer content from 40-100 wt. % and with an NCO-content of 25 wt. % to 35 wt.-%.

5. The method according to claim 2 , wherein in at least one of the first and/or second profile the reinforcement fabric comprises glass fibers, carbon fibers and/or aramid fibers.

6. The method according to claim 2 , wherein in at least one of the first and/or second profile the reinforcement fabric is a biaxial non-woven fabric with at least a portion of the fibers oriented in an angle of 40° to 50° with respect to the longitudinal axis of the foam core.

7. The method according to claim 2 , wherein in at least one of the first and/or second profile the reinforcement fabric is in a one-part form.

8. The method according to claim 2 , wherein in at least one of the first and/or second profile the foam core is bonded to the reinforcement fabric without an additional adhesive.

9. The method according to claim 1 , wherein the foam comprises a polyurethane foam, an epoxy resin foam, a polyester resin foam, an expanded polystyrene foam and/or an expanded polypropylene foam.

10. A method of manufacturing a composite panel, the method comprising:

providing a first textile layer;

applying a first adhesive to at least a portion of the first textile layer;

forming a plurality of first profiles adjacent to each other onto at least a portion of the first textile layer which has been contacted with the first adhesive, wherein:

each of the first profiles comprises a foam core and a reinforcement fabric located on the foam core, and

each of the first profiles is obtained by bonding a respective foam core to a pre-formed reinforcement fabric;

applying, at least once, at least one second profile between two first profiles in such a manner that a foam is provided between two first profiles, wherein the foam, when applied, is not completely cured and still possesses a residual tackiness to the reinforcement fabric such that it bonds to the reinforcement fabric with superficial contact which does not extend into the depth of the fabric;

testing the foam to determine tackiness; and

providing a second textile layer onto the at least one second profile.

11. The method of claim 10 , wherein the step of testing further comprises:

repeatedly testing with a wooden rod.