Composites formed from an absorptive filler and a polyurethane
View Patent ↗Composite materials and methods for their preparation are described herein. The composite materials can comprise a polyurethane and an absorptive filler. The polyurethane can be formed from the reaction of at least one isocyanate selected from the group consisting of diisocyanates, polyisocyanates, and combinations thereof, and one or more isocyanate-reactive monomers. The one or more isocyanate-reactive monomers can comprise at least one polyol and a first isocyanate-reactive monomer which includes one or more isocyanate-reactive functional groups and a moiety configured to associate with the absorptive filler.
1. A composite comprising:
an absorptive filler comprising fly ash having at least 0.1%, by weight of the fly ash, of an organic carbon, and
a polyurethane formed by a reaction of at least one isocyanate selected from the group consisting of diisocyanates, polyisocyanates, and combinations thereof, and one or more isocyanate-reactive monomers comprising a Mannich polyol, in the presence of an amine catalyst,
wherein the Mannich polyol is in an amount from 10% to 50% by weight, based on the total weight of the one or more isocyanate-reactive monomers, and associates with the absorptive filler through a nitrogen-containing moiety; and
wherein the composite has a tack-free time that varies less than 10% regardless of the fly ash used.
2. The composite of claim 1 , wherein the absorptive filler is present in an amount from 40% to 90% by weight, based on the total weight of the composite.
3. The composite of claim 1 , wherein the nitrogen-containing moiety comprises an amine.
4. The composite of claim 1 , wherein the Mannich polyol comprises an alkanolamine.
5. The composite of claim 4 , wherein the alkanolamine comprises a dialkanolamine which includes two hydroxy-substituted C1-C12 alkyl groups, or a trialkanolamine which includes three hydroxy-substituted C1-C12 alkyl groups.
6. The composite of claim 1 , wherein the Mannich polyol comprises an alkoxylated polyamine derived from a polyamine and an alkylene oxide.
7. The composite of claim 1 , wherein the Mannich polyol is derived from a substituted or unsubstituted phenol and an alkanolamine.
8. The composite of claim 7 , wherein the Mannich polyol is further derived from an alkylene oxide.
9. The composite of claim 1 , wherein the Mannich polyol is from 10% to 40% by weight of the one or more isocyanate-reactive monomers.
10. The composite of claim 1 , wherein the one or more isocyanate-reactive monomers further comprises a highly reactive polyol, wherein at least 75% of the hydroxyl groups in the highly reactive polyol comprise primary hydroxyl groups.
11. The composite of claim 10 , wherein the highly reactive polyol is from 10% to 40% by weight of the one or more isocyanate-reactive monomers.
12. The composite of claim 1 , wherein the one or more isocyanate-reactive monomers further comprises a polyester polyol, a polyether polyol, or a combination thereof.
13. The composite of claim 12 , wherein the polyester polyol comprises an aromatic polyester polyol.
14. A method of preparing a composite material, comprising:
mixing (1) an absorptive filler comprising fly ash having at least 0.1%, by weight of the fly ash, of an organic carbon; (2) at least one isocyanate selected from the group consisting of diisocyanates, polyisocyanates, and combinations thereof; (3) one or more isocyanate-reactive monomers comprising a Mannich polyol; and (4) an amine catalyst; and
allowing the at least one isocyanate and the one or more isocyanate-reactive monomers to react in the presence of the absorptive filler and the amine catalyst to form the composite material,
wherein the Mannich polyol is in an amount from 10% to 50% by weight, based on the total weight of the one or more isocyanate-reactive monomers, and associates with the absorptive filler through a nitrogen-containing moiety; and
wherein the composite material has a tack-free time that varies less than 10% regardless of the fly ash used.
15. The composite of claim 1 , wherein the one or more isocyanate-reactive monomers comprise an alkylene-oxide capped Mannich polyol.
16. The composite of claim 1 , wherein the amine catalyst is selected from 1,4-diazabicyclo[2.2.2]octane, triethylenediamine, and tetramethylbutanediamine.
17. A composite comprising:
40-90% by weight of the composite of fly ash, the fly ash comprising at least 0.1% by weight of the fly ash of an organic carbon, and
a polyurethane formed from a reaction of at least one isocyanate selected from the group consisting of diisocyanates, polyisocyanates, and combinations thereof, and one or more isocyanate-reactive monomers comprising a Mannich polyol and an aromatic polyester polyol, in the presence of an amine catalyst,
wherein the Mannich polyol is in an amount from 10% to 50% by weight, based on the total weight of the one or more isocyanate-reactive monomers, and associates with the fly ash through a nitrogen-containing moiety; and
wherein the composite has a tack-free time that varies less than 10% regardless of the fly ash used.
18. The composite of claim 1 , wherein the Mannich polyol is from 10% to 25% by weight of the one or more isocyanate-reactive monomers.
19. The composite of claim 17 , wherein the Mannich polyol is from 10% to 25% by weight of the one or more isocyanate-reactive monomers.