METHOD FOR IMPROVING THE WELDABILITY OF HOT STAMPING PARTS
A method for improving the weldability of hot stamping parts improving weldability of hot stamping parts with degraded weldability due to surface oxides is provided. In accordance with an embodiment of the present invention, a method for improving the weldability of hot stamping parts comprises: selecting a welding region in a hot stamping part; removing surface oxide of the welding region; and performing welding on a welding region on a hot stamping part with surface oxide removed.
1 . A method for improving the weldability of hot stamping parts, comprising:
selecting a welding region in a hot stamping part;
removing surface oxide layer of the welding region; and
performing welding on a welding region on a hot stamping part with the surface oxide removed.
2 . A method for improving the weldability of hot stamping parts according to claim 1 , wherein the hot stamping part is a material of Al—Si plated steel sheet.
3 . A method for improving the weldability of hot stamping parts according to claim 1 , wherein the hot stamping part is a material of Al—Si plated steel sheet and welding is performed on the welding region using projection welding.
4 . A method for improving the weldability of hot stamping parts according to claim 1 , wherein the hot stamping part is a material of Al—Si plated steel sheet and welding is performed on the welding region using projection welding, and a grinder is used or a laser grinder is used when removing surface oxide.
5 . A method for improving the weldability of hot stamping parts, comprising:
selecting a welding region in a hot stamping part;
removing surface oxide layer of the welding region;
removing remnant of oxide layer and portion of plating layer of the welding region; and
performing welding on a welding region on a hot stamping part with remnant of oxide layer and portion of plating layer removed.
6 . A method for improving the weldability of hot stamping parts according to claim 5 , wherein the hot stamping part is a material of Al—Si plated steel sheet.
7 . A method for improving the weldability of hot stamping parts according to claim 5 , wherein the hot stamping part is a material of Al—Si plated steel sheet and welding is performed on the welding region using projection welding.
8 . A method for improving the weldability of hot stamping parts according to claim 5 , wherein the hot stamping part is a material of Al—Si plated steel sheet and welding is performed on the welding region using projection welding, and a grinder is used or laser grinder is used when removing surface oxide layer and removing remnant of oxide layer and portion of plating layer.
9 . A method for improving the weldability of hot stamping parts, comprising:
selecting a welding region in a hot stamping part;
removing surface oxide of the welding region;
removing remnant of oxide layer and portion of plating layer of the welding region;
removing entire plating layer of the welding region; and
performing welding on a welding region on a hot stamping part with remnant of oxide layer and entire plating layer removed.
10 . A method for improving the weldability of hot stamping parts according to claim 9 , wherein the hot stamping part is a material of Al—Si plated steel sheet.
11 . A method for improving the weldability of hot stamping parts according to claim 9 , wherein the hot stamping part is a material of Al—Si plated steel sheet and welding is performed on the welding region using projection welding.
12 . A method for improving the weldability of hot stamping parts according to claim 5 , wherein the hot stamping part is a material of Al—Si plated steel sheet and welding is performed on the welding region using projection welding, and a grinder is used or laser grinder is used when removing surface oxide layer and removing remnant of oxide layer and portion of plating layer and removing entire plating layer.