Rolled steel bar for hot forging
View Patent ↗A rolled steel bar has a composition consisting, by mass percent, of C: 0.27 to 0.37%, Si: 0.30 to 0.75%, Mn: 1.00 to 1.45%, S: 0.008% or more and less than 0.030%, Cr: 0.05 to 0.30%, Al: 0.005 to 0.050%, V: 0.200 to 0.320%, and N: 0.0080 to 0.0200%, the balance being Fe and impurities. The contents of P, Ti and O in the impurities are, by mass percent, P: 0.030% or less, Ti: 0.0040% or less, and O: 0.0020% or less. Y1 expressed by the formula <1> is 1.05 to 1.18. Y1=C+(1/10)Si+(1/5)Mn+(5/22)Cr+1.65V−(5/7)S <1>. C, Si, Mn, Cr, V, and S in the formula represent mass percent of the elements. A hot-forged part having a tensile strength of 900 MPa or higher and a transverse endurance ratio of 0.47 can be obtained by the rolled steel bar.
1. A rolled steel bar for a hot-forged part having a chemical composition consisting, by mass percent, of C: 0.27 to 0.37%, Si: 0.30 to 0.75%, Mn: 1.00 to 1.45%, S: 0.008% or more and less than 0.030%, Cr: 0.05 to 0.30%, Al: 0.005 to 0.050%, V: 0.200 to 0.320%, and N: 0.0080 to 0.0200%, the balance being Fe and impurities, wherein
the hot-forged part having a transverse tensile strength of 900 MPa or higher and a transverse endurance ratio of 0.47 or higher, and wherein,
the contents of P, Ti and O in the impurities are, by mass percent, P: 0.030% or less, Ti: 0.0040% or less, and O: 0.0020% or less; and
Y1 expressed by the following formula <1> is 1.05 to 1.18,
Y1=C+(1/10)Si+(1/5)Mn+(5/22)Cr+1.65V−(5/7)S <1>
where, C, Si, Mn, Cr, V, and S in the above formula <1> represent, respectively, the content by mass percent of each of the elements.
2. A rolled steel bar for a hot forged part having a chemical composition consisting, by mass percent, of C: 0.27 to 0.37%, Si: 0.30 to 0.75%, Mn: 1.00 to 1.45%, S: 0.008% or more and less than 0.030%, Cr: 0.05 to 0.30%, Al: 0.005 to 0.050%, V: 0.200 to 0.320%, and N: 0.0080 to 0.0200%, and one or more elements selected from the group consisting of Cu: 0.30% or less, Ni: 0.30% or less, and Mo: 0.10% or less, the balance being Fe and impurities, wherein
the hot-forged part having a transverse tensile strength of 900 MPa or higher and a transverse endurance ratio of 0.47 or higher, and wherein,
the contents of P, Ti and O in the impurities are, by mass percent, P: 0.030% or less, Ti: 0.0040% or less, and O: 0.0020% or less; and
Y2 expressed by the following formula <2> is 1.05 to 1.18,
Y2=C+(1/10)Si+(1/5)Mn+(5/22)Cr+1.65V−(5/7)S+(1/5)Cu+(1/5)Ni+(1/4)Mo <2>
where, C, Si, Mn, Cr, V, S, Cu, Ni, and Mo in the above formula <2> represent, respectively, the content by mass percent.