Hot-rolled steel sheet for nitriding, cold-rolled steel sheet for nitriding excellent in fatigue strength, manufacturing method thereof, and automobile part excellent in fatigue strength using the same
View Patent ↗A hot-rolled steel sheet for nitriding or a cold-rolled steel sheet for nitriding, in which a dislocation density within 50 μm in the sheet thickness direction from the surface is not less than 2.0 times nor more than 10.0 times as compared to a dislocation density at the position of ¼ in the sheet thickness direction; and a method of manufacturing the same. The manufacturing method comprises, on a hot-rolled steel sheet or a cold-rolled steel sheet, performing pickling, and then performing skin pass rolling under the condition that a reduction ratio is 0.5 to 5.0% and FIT, defined as a ratio of a line load F (kg/mm) of a rolling mill load divided by a sheet width of the steel sheet and a load T (kg/mm 2 ) per unit area to be applied in the longitudinal direction of the steel sheet, is 8000 or more.
1. A steel sheet for nitriding, comprising:
in mass %,
C: not less than 0.0002% and not more than 0.07%;
Si: not less than 0.0010% and not more than 0.50%;
Mn: not less than 0.10% and not more than 1.33%;
P: not less than 0.003% and not more than 0.02%;
S: not less than 0.001% and not more than 0.02%;
Cr: greater than 0.80% and 1.20% or less;
Al: not less than 0.10% and not more than 0.50%;
V: not less than 0.05% and not more than 0.10%;
Ti: not less than 0.005% and not more than 0.10%;
B: not less than 0.0001% and not more than 0.0015%; and
a balance comprising Fe and inevitable impurities, wherein:
a dislocation density within 50 μm from a surface of the steel sheet in a sheet thickness direction is not less than 2.0 times and not more than 10.0 times a dislocation density at a position which is located at ¼ of a sheet thickness in the sheet thickness direction.
2. The steel sheet for nitriding according to claim 1 , further comprising:
one or both of, in mass %,
Mo: not less than 0.001 and not more than 0.20%; and
Nb: not less than 0.001 and not more than 0.050%.
3. A steel sheet for nitriding, comprising:
in mass %,
C: not less than 0.0002% and not more than 0.07%;
Si: not less than 0.0010% and not more than 0.50%;
Mn: not less than 0.10% and not more than 1.33%;
P: not less than 0.003% and not more than 0.02%;
S: not less than 0.001% and not more than 0.02%;
Cr: greater than 0.80% and 1.20% or less;
Al: not less than 0.10% and not more than 0.50%;
V: not less than 0.05% and not more than 0.10%;
Ti: not less than 0.005% and not more than 0.10%;
B: not less than 0.0001% and not more than 0.0015%; and
a balance comprising Fe and inevitable impurities,
wherein:
a dislocation density within 50 μm from a surface of the steel sheet in a sheet thickness direction is not less than 2.0 times and not more than 10.0 times a dislocation density at a position which is located at ¼ of a sheet thickness in the sheet thickness direction, and
the sheet thickness of the steel sheet is 1.6 to 5.0 mm.