Material for friction components of disc brakes
View Patent ↗The invention illustrates a material for friction components of disc brakes comprising between 1% and 8% by weight of at least one preceramic resin and between 2% and 10% by weight of at least one organic resin. It also illustrates a friction component for a disc brake, a disc brake, and a process for producing such a material.
1. A material for friction components of disc brakes consisting of:
a mixture between 1% and 8% by weight of a preceramic silicone resin and between 2% and 10% by weight of an organic resin selected from a phenolic resin, an acrylic resin, and an epoxy resin; and
at least one catalyst, at least one abrasive agent, at least one lubricant, at least one metal, and at least one damping agent.
2. The material for friction components according to claim 1 , wherein a total amount of preceramic silicone resin and organic resin is less than or equal to 12% by weight.
3. The material for friction components according to claim 1 , comprising between 2% and 6% by weight of preceramic silicone resin and between 4% and 8% by weight of organic resin.
4. The material for friction components according to claim 1 , comprising 2% by weight of preceramic silicone resin and 7% by weight of organic resin.
5. The material for friction components according to claim 1 , wherein said preceramic silicone resin comprises at least one silicone resin.
6. The material for friction components according to claim 5 , wherein said silicone resin is a siloxane resin.
7. The material for friction components according to claim 6 , wherein said siloxane resin is a polysilsesquioxane resin.
8. The material for friction components according to claim 1 , wherein said organic resin is a phenolic resin.
9. A friction component for disc brakes comprising a material consisting of:
a mixture between 1% and 8% by weight of a preceramic silicone resin and between 2% and 10% by weight of an organic resin selected from a phenolic resin, an acrylic resin, and an epoxy resin; and
at least one catalyst, at least one abrasive agent, at least one lubricant, at least one metal, and at least one damping agent.
10. The friction component according to claim 9 , comprising at least one pad for a disc brakes.
11. A disc brake comprising at least two pads according to claim 10 and a caliper for a disc brake comprising thrusting means suitable for clamping said at least two pads against a braking face of a brake disc.
12. A process for producing a material for friction components of disc brakes comprising the following steps:
providing between 1% and 8% by weight of a preceramic silicone resin;
providing between 2% and 10% by weight of an organic resin selected from a phenolic resin, an acrylic resin, and an epoxy resin;
mixing the preceramic silicone resin and the organic resin;
forming a mixture consisting of: the preceramic silicone resin, the organic resin, at least one catalyst, at least one abrasive agent, at least one lubricant, at least one metal, and at least one damping agent;
moulding and polymerising the mixture so as to obtain a semifinished product; and
firing the semifinished product.
13. The process for producing a material for friction components of disc brakes according to claim 12 , wherein a total amount of preceramic silicone resin and organic resin is less than or equal to 12% by weight.
14. The process for producing a material for friction components of disc brakes according to claim 12 , wherein the preceramic silicone resin is between 2% and 6% by weight, and the organic resin is between 4% and 8% by weight.
15. The process for producing a material for friction components of disc brakes according to claim 12 , wherein the preceramic silicone resin is 2% by weight and the organic resin is 7% by weight.
16. The process for producing a material for friction components of disc brakes according to claim 12 , wherein the preceramic silicone resin comprises at least one silicone resin.
17. The process for producing a material for friction components of disc brakes according to claim 12 , wherein the preceramic silicone resin comprises a siloxane resin.
18. The process for producing a material for friction components of disc brakes of claim 12 , wherein the preceramic silicone resin comprises a polysilsesquioxane resin.
19. The process for producing a material for friction components of disc brakes of claim 12 , wherein the organic resin is a phenolic resin.