Ethylene-propylene-maleic acid anhydride copolymer as impact modifier in glass-fiber reinforced, flame-retardant polycarbonates for the EE sector

1. A flame-resistant, thermoplastic moulding composition comprising:

A) 41.500 to 94.749 parts by wt. of at least one aromatic polycarbonate,

B) 0.001 to 1.000 part by wt. of at least one flameproofing agent selected from the group consisting of alkali metal and alkaline earth metal salts of aliphatic or aromatic sulfonic acid, sulfonamides and sulfonimide derivatives,

C) 0.20 to 1.50 parts by wt. of at least one rubber-free anhydride-modified alpha-olefin terpolymer,

D) 5.0 to 40.0 parts by wt. of at least one glass fibre,

E) 0.00 part by wt. to 1.00 part by wt. of at least one mould release agent,

F) 0.05 part by wt. to 5.00 parts by wt. of at least one antidripping agent,

G) 0.0-10.0 parts by wt. of a further additive selected from the group consisting of antioxidants, heat stabilizers, optical brighteners and light-scattering agents,

wherein the sum of the parts by weight of components A) to G) adds up to 100 parts by weight.

2. The moulding composition according to claim 1 , wherein the composition comprises component D) in an amount of from 7.0 to 20.0 parts by wt.

3. The moulding composition according to claim 1 , wherein the composition comprises component G) in an amount of from 0.20 to 3.0 parts by wt.

4. The moulding composition according to claim 1 , wherein the composition comprises component C) in an amount of from 0.40 to 0.60 parts by wt.

5. The moulding composition according to claim 1 , wherein the anhydride is selected from the group consisting of maleic anhydride, phthalic anhydride, fumaric anhydride, itaconic anhydride and mixtures thereof.

6. The moulding composition according to claim 5 , wherein the anhydride is maleic anhydride.

7. The moulding composition according to claim 5 , wherein the alpha-olefin terpolymer comprises units selected from the group consisting of ethylene, 1-propene, 1-butene, 1-isobutene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 1-nonene, 1-decene, 1-undecene, 1-dodecene, 1-tridecene, 1-tetradecene, 1-octadecene, 1-nonadecene and mixtures thereof.

8. The moulding composition according to claim 5 , wherein the at least one rubber-free anhydride-modified terpolymer comprises

E1) 90.0-98.0 wt. % of terpolymer and

E2) 2.0-10.0 wt. % of anhydride.

9. The moulding composition according to claim 1 , wherein the terpolymer consists of units of ethylene, 1-propene and 1-octene.

10. The moulding composition according to claim 8 , wherein the olefinic part E1) of the anhydride-modified terpolymer is characterized in that

the ethylene content is 96.0-80.0 wt. %;

the propylene content is 2.0-10.0 wt. %; and

the octene content is 2.0-10.0 wt. %.

11. The moulding composition according to claim 1 , wherein the at least one rubber-free anhydride-modified terpolymer has a molecular weight Mw of 2,000-10,000 g/mol.

12. The moulding composition according to claim 1 , wherein the at least one glass fibre is a cut glass fibre.

13. The moulding composition according to claim 12 , wherein the at least one cut glass fibre is produced from E- or C-glass and has a fibre diameter of from 5 to 25 μm.

14. The moulding composition according to claim 1 , wherein the at least one flameproofing agent is selected from the group consisting of sodium and potassium perfluorobutane-sulfate, sodium and potassium perfluorooctane-sulfate, sodium and potassium diphenyl sulfone-sulfonate, sodium and potassium 2,4,6-trichlorobenzoate, N-(p-tolylsulfonyl)-p-toluenesulfimide potassium salt and N—(N′-benzylaminocarbonyl)-sulfanylimide potassium salt.

15. A method for the production of a thin-walled housing part or a switch box comprising utilizing the moulding composition according to claim 1 , wherein the thin-walled housing part or the switch box has a flameproofing of UL94 V0 at a minimum of 1 mm wall thickness and an impact strength of at least 110 kJ/mm 2 at room temperature (RT) according to ISO 179/1eU.

16. The moulding composition according to claim 13 , wherein the at least one cut glass fibre has a length before compounding of from 3 mm to 6 mm.