Continuous synthesis of high quantum yield InP/ZnS nanocrystals
View Patent ↗The invention relates to a continuous-flow synthesis process for the preparation of high quality indium phosphide/zinc sulfide core/shell semiconduting nanocrystals in particular quantum dots (QD) conducted in a micro-reaction system comprising at least one mixing chamber connected to one reaction chamber.
1. A continuous-flow method for preparing InP/ZnS nanoparticles conducted in a micro-reaction system comprising at least one mixing chamber connected to one reaction chamber, said method comprising:
preparing an indium precursor solution by mixing an indium salt, a fatty protic alkylamine, a fatty alkylacid, and zinc carboxylate with an inert solvent and heating up to 50-200° C. to get a clear solution under water and oxygen free atmosphere;
preparing a phosphine precursor solution comprising tris(trimethylsilyl) phosphine in the inert solvent under water and oxygen free atmosphere;
injecting the indium precursor solution in excess to the phosphine precursor solution into the mixing chamber to obtain a reaction mixture, wherein the mixing chamber is a magnetic mixing micro-chamber with a volume in the range of 10 mm 3 to 10,000 mm 3 , and wherein the injecting is at a flow rate from 0.1 ml/min to 10 ml/min;
forwarding and heating the reaction mixture at a temperature from 160 to 320° C., within the reaction chamber until InP core suspension is obtained;
forwarding the core suspension into a mixing chamber and injecting a shell precursor solution comprising a Zn source and a S source to the core suspension and capping ligands into the mixing chamber;
forwarding and heating the suspension at a temperature from 160 to 320° C. for shell preparation within the reaction chamber; and cooling.
2. The continuous-flow method of claim 1 , wherein the Zn source and the S source is a single source.
3. The continuous-flow method of claim 1 , wherein the mixing chamber is a magnetic mixing micro-chamber with a volume in the range of 30 mm 3 to 70 mm 3 .
4. The continuous-flow method of claim 1 , wherein the reaction chamber has an inner diameter in the range of 0.1 mm and 2 mm and a length in the range of 0.5 m to 20 m.
5. The continuous-flow method of claim 1 , wherein the forwarding and heating of the reaction mixture within the reaction chamber until InP core suspension is obtained is at a temperature from 200 to 280° C.
6. The continuous-flow method of claim 1 , wherein all operations are completed in less than one hour.