Thermoplastic elastomer composition having low hardness, and diaphragm comprising same
A thermoplastic elastomer composition of the present invention comprises (A) 30 to 40% by weight of a block terpolymer of an aromatic vinyl compound and alkene or a conjugated diene-based compound; (B) 25 to 50% by weight of a paraffin oil; (C) 1 to 5% by weight of a polyolefin-based resin; (D) 5 to 20% by weight of an inorganic additive; and (E) 5 to 15% by weight of a polyphenylene ether-based resin. The thermoplastic elastomer composition, which has a surface hardness of 0.1 to 40 A (shore A), shows excellent low hardness and has improved physical properties at high temperature, particularly, flexibility, restoring force at high temperatures, and the like.
1. A thermoplastic elastomer composition comprising:
(A) 30 to 40% by weight of a block terpolymer of an aromatic vinyl compound with alkene or a conjugated diene-based compound;
(B) 25 to 50% by weight of a paraffin oil;
(C) 2 to 4% by weight of a polyolefin-based resin;
(D) 5 to 20% by weight of an inorganic additive; and
(E) 5 to 15% by weight of a polyphenylene ether-based resin,
wherein the amounts of (A), (B), (C), (D), and (E) are based on 100% by weight of the thermoplastic elastomer composition formed of (A)+(B)+(C)+(D)+(E), and
(F) 0.01 to 0.4 parts by weight of silicone-based resin based on 100 parts by weight of the thermoplastic elastomer composition formed of (A)+(B)+(C)+(D)+(E), wherein the silicone-based resin (F) is a master batch composition of a silicone resin and the polyolefin-based resin,
wherein the silicone-based resin (F) includes a silicone resin comprising a polymer of hexamethyl cyclotrisiloxane, octamethyl cyclotetrasiloxane, decamethyl cyclopentasiloxane, dodecamethyl cyclohexasiloxane, trimethyl triphenylcyclotrisiloxane, and/or tetramethyl tetraphenylcyclotetrasiloxane, and
wherein the thermoplastic elastomer composition has a permanent elongation set (%) of 1.4 to 2.1 measured at 23° C. in accordance with KS M 6518.
2. The thermoplastic elastomer composition according to claim 1 , wherein the silicone-based resin includes the silicone resin and the polyolefin-based resin in a weight ratio of 1:0.5 to 1:1.5.
3. The thermoplastic elastomer composition according to claim 1 , wherein the block terpolymer is in an A-B-A′ form, the A and A′ blocks are hard segments, the B block is a soft segment, and the block terpolymer includes 20 to 35% by weight of the A and A′ blocks and 65 to 80% by weight of the B block.
4. The thermoplastic elastomer composition according to claim 3 , wherein the A and A′ blocks are aromatic vinyl polymers, and the B block is an olefin or conjugated diene-based polymer.
5. The thermoplastic elastomer composition according to claim 1 , wherein the block terpolymer (A) comprises a styrene-ethylene/butylene-styrene (SEBS) block copolymer, a styrene-ethylene/propylene-styrene (SEPS) block copolymer, a styrene-isoprene-styrene (SIS) block copolymer, a styrene-ethylene/(ethylene/propylene)-styrene (SEEPS) block copolymer, or a combination thereof.
6. The thermoplastic elastomer composition according to claim 1 , wherein the block terpolymer (A) has a weight average molecular weight of 140,000 to 180,000 g/mol.
7. The thermoplastic elastomer composition according to claim 1 , wherein the paraffin oil has a kinematic coefficient of viscosity of 95 to 215 cst (based on 40° C.).
8. The thermoplastic elastomer composition according to claim 1 , comprising the block terpolymer (A) and the paraffin oil (B) in a ratio of 1:1 to 1:2.5.
9. The thermoplastic elastomer composition according to claim 1 , wherein the polyolefin-based resin (C) has a melting index (230° C., 2.16 kg) of 20 to 40 g/10 min.
10. The thermoplastic elastomer composition according to claim 1 , wherein the polyolefin-based resin (C) comprises a polyethylene resin, a polypropylene resin, a polybutylene resin, an ethylene-propylene copolymer resin, an ethylene-vinyl alcohol copolymer resin, or a combination thereof.
11. The thermoplastic elastomer composition according to claim 1 , wherein the inorganic additive (D) has a particle size of 0.01 to5 μm.
12. The thermoplastic elastomer composition according to claim 1 , wherein the inorganic additive (D) comprises calcium carbonate, talc, clay, silica, mica, titanium dioxide, carbon black, graphite, wollastonite, nanosilver, or a combination thereof.
13. The thermoplastic elastomer composition according to claim 1 , wherein the polyphenylene ether-based resin (E) has a weight average molecular weight of 20,000 to 40,000 g/mol.
14. The thermoplastic elastomer composition according to claim 1 , wherein the thermoplastic elastomer composition further comprises additives selected from antimicrobial agents, thermal stabilizers, antioxidant, releasing agents, photo stabilizers, surfactants, coupling agents, plasticizers, admixtures, coloring agents, stabilizers, lubricants, antistatic agents, color mixing agents, resistants, weatherproof agents, ultraviolet absorbers, ultraviolet blocking agents, flame retardants, fillers, nucleating agents, adhesive agents, adhesives, and combinations thereof.
15. A molded article prepared by the thermoplastic elastomer composition of claim 1 , wherein the molded article has a surface hardness of 0.1 to 40 A (shore A).
16. The molded article according to claim 15 , wherein the molded article has a tensile strength of 50 kgf/cm 2 or more measured in accordance with ASTM D638 at 23° C.; a tensile strength of 10 to 25 kgf/cm 2 measured in accordance with ASTM D638 at 100° C.; and a permanent elongation and extension rate of 5 to 13% at 100° C. measured in accordance with a type 3 sample of KS M 6518.
17. The molded article according to claim 15 , wherein the molded article is a diaphragm of a washing machine.
18. The thermoplastic elastomer composition according to claim 1 , wherein a molded article prepared by the thermoplastic elastomer composition of claim 1 has a surface hardness of 0.1 to 40 A (shore A) measured in accordance with KSM 6518.
19. The thermoplastic elastomer composition according to claim 18 , wherein a molded article prepared by the thermoplastic elastomer composition of claim 1 has less than 2 g abrasion amount after repeating 12,000 times measured in accordance with ASTM D4060.
20. The thermoplastic elastomer composition according to claim 19 , wherein a molded article prepared by the thermoplastic elastomer composition of claim 1 has 1 mg to 1000 mg abrasion amount after repeating 12,000 times measured in accordance with ASTM D4060.
21. The thermoplastic elastomer composition according to claim 1 , comprising 0.01 to 0.35 parts by weight of the silicon-based resin (F), wherein a molded article prepared by the thermoplastic elastomer composition of claim 1 has a surface hardness of 0.1 to 37 A (shore A) measured in accordance with KSM 6518.
22. The thermoplastic elastomer composition according to claim 1 , wherein the silicone-based resin (F) includes a silicone resin comprising a polymer of hexamethyl cyclotrisiloxane, octamethyl cyclotetrasiloxane, decamethyl cyclopentasiloxane, and/or dodecamethyl cyclohexasiloxane.