Ultra high molecular weight polyethylene multifilament yarn
The invention relates to a multifilament yarn containing n filaments, wherein the filaments are obtained by spinning an ultra-high molecular weight polyethylene (UHMWPE), said yarn having a tenacity (Ten) as expressed in cN/dtex of Ten(cN/dtex)=f×n −0.05 ×dpf −0.15 , wherein Ten is at least 39 cN/dtex, n is at least 25, f is a factor of at least 58 and dpf is the dtex per filament.
1. A multifilament yarn comprising a number n of filaments, wherein the filaments are obtained by spinning an ultra-high molecular weight polyethylene (UHMWPE), said yarn having a tenacity (Ten) as expressed in cN/dtex according to Formula 1:
Ten(cN/dtex)= f×n −0.05 ×dpf −0.15 (Formula 1)
wherein Ten is at least 39 cN/dtex, n is at least 100, f is a factor of at least 58 and dpf is the dtex per filament.
2. The yarn according to claim 1 wherein the factor f is at least 60.0.
3. The yarn according to claim 1 wherein the number n of filaments is at least 200.
4. The yarn according to claim 1 wherein the dpf is at least 0.8.
5. The yarn according to claim 1 , wherein the number n of filaments is at least 400.
6. The yarn according to claim 1 , wherein the dpf is at least 1.3.
7. Ropes and cordages comprising the multifilament according to claim 1 .
8. A reinforcing element suitable for reinforcing products, the element comprising the multifilament according to claim 1 .
9. A medical device comprising the multifilament according to claim 1 .
10. A composite article comprising the multifilament according to claim 1 .
11. A composite article comprising at least one mono-layer which comprises the multifilament yarn according to claim 1 .
12. A multi-layered composite article containing a plurality of unidirectional mono-layers, said mono-layers comprising the multifilament according to claim 1 , wherein the direction of the yarn in each mono-layer is rotated with an angle with respect to the direction of the yarn in an adjacent mono-layer.
13. A product comprising the multifilament according to claim 1 , wherein the product is selected from the group consisting of fishing lines and fishing nets, ground nets, cargo nets and curtains, kite lines, dental floss, tennis racquet strings, canvas, tent canvas, nonwoven cloths, webbings, battery separators, capacitors, pressure vessels, hoses, umbilical cables, electrical, optical fiber, and signal cables, automotive equipment, power transmission belts, building construction materials, cut and stab resistant and incision resistant articles, protective gloves, composite sports equipment, skis, helmets, kayaks, canoes, bicycles and boat hulls and spars, speaker cones, high performance electrical insulation, radomes, sails and geotextiles.
14. A panel comprising a plurality of sheets containing the multifilament yarn of claim 1 , wherein each sheet comprises at least two monolayers.
15. The panel of claim 14 , wherein the panel has an Eabs (J/[kg/m 2 ]) of at least 170 against an AK47 FMJ MSC projectile, said Eabs being determined for an areal density of the panel of about 15.5 kg/m 2 .
16. The panel of claim 14 , wherein the panel has an Eabs (J/[kg/m 2 ]) of at least 370 against a 0.357 Magnum JSP projectile, said Eabs being determined for an areal density of the panel of about 3.1 Kg/m 2 .
17. The panel of claim 16 , wherein the panel has an Eabs (J/[kg/m 2 ]) against a 17 grain FSP projectile of at least 35, said Eabs being determined for an areal density of the panel of about 3.1 Kg/m 2 .