Polymer dispersions, their preparation and use
View Patent ↗In a multi-stage emulsion polymerization process, a first monomer composition comprising from about 60 weight percent to about 95 weight percent of at least one vinyl ester, and from about 5 weight percent to about 40 weight percent ethylene is polymerized in a first stage under ethylene pressure to produce a first stage product having a T g of less than 20° C. Then, in a second stage, a second monomer composition comprising at least 95 weight percent of a meth(acrylic)ester or a mixture of at least two different (meth)acrylic esters is polymerized in the presence of said first stage product, wherein the (meth)acrylic ester(s) is selected such that the polymer produced by said second monomer composition has a T g of 5 to 90° C.
1. An emulsion polymerization process for making binder emulsions, comprising:
(a) polymerizing, in a first stage and under ethylene pressure, a first monomer composition comprising from about 60 weight percent to about 95 weight percent of at least one vinyl ester, from about 5 weight percent to about 40 weight percent ethylene, and at least one of an epoxy-functional, ethylenically unsaturated compound or a silicone-functional, ethylenically unsaturated compound, to produce a first stage product having a T g of less than 25° C.; and
(b) polymerizing, in a second stage and in the presence of said first stage product, a second monomer composition comprising at least 95 weight percent of ethyl methacrylate, butyl methacrylate or mixtures thereof, or a mixture of methyl methacrylate with an acrylic ester selected from the group consisting of butyl acrylate and ethylhexyl acrylate, such that the polymer produced by said second monomer composition has a T g from 5 to 90° C.
2. An emulsion polymerization process according to claim 1 , wherein the copolymer produced by said first monomer composition has a lower T g than the polymer produced by said second monomer composition.
3. An emulsion polymerization process according to claim 1 , wherein the vinyl ester is vinyl acetate.
4. An emulsion polymerization process according to claim 1 , wherein the first monomer composition further comprises from 0.05 weight percent to about 5 weight percent of at least one of an ethylenically unsaturated mono- and/or dicarboxylic acid, an ethylenically unsaturated sulfonic acid, an ethylenically unsaturated phosphoric acid, an ethylenically unsaturated phosphonic acid, and an amide of an ethylenically unsaturated mono- and/or dicarboxylic acid.
5. An emulsion polymerization process according to claim 1 , wherein the second monomer composition further comprises from about 0.05 weight percent to about 5 weight percent of at least one of an ethylenically unsaturated mono- and/or dicarboxylic acid, an ethylenically unsaturated sulfonic acid, an ethylenically unsaturated phosphoric acid, an ethylenically unsaturated phosphonic acid, and an amide of an ethylenically unsaturated mono- and/or dicarboxylic acid.
6. An emulsion polymerization process according to claim 1 , wherein the copolymer produced by said first monomer composition has a glass transition temperature in the range of about 5° C. to about 15° C.
7. An emulsion polymerization process according to claim 1 , wherein the polymer produced by said second monomer composition has a glass transition temperature in the range of from about 10° C. to about 75° C.
8. An emulsion polymerization process according to claim 1 , wherein the weight ratio of the first monomer composition to the second monomer composition is in the range 60:40 to 95:5.
9. An emulsion polymerization process according to claim 1 , wherein at least one of the first and second monomer compositions additionally comprise an anionic emulsifier and/or a nonionic emulsifier.
10. A polymer emulsion produced by the process of claim 1 .
11. A paint composition comprising the polymer emulsion of claim 10 and at least one pigment.
12. The paint composition of claim 11 and having a minimum film forming temperature of less than 5° C.
13. The paint composition of claim 11 , wherein the paint is a wood protection paint, a gloss paint or an interior paint.
14. A coating produced from paint composition of claim 11 and having a water take up value (w) of less than 0.15 kg/(m 2 h 0.5 ).
15. A plaster composition comprising the polymer emulsion of claim 10 and at least one filler.
16. A thermal insulation system comprising the plaster composition of claim 15 .
17. An emulsion polymerization process according to claim 1 , wherein the polymer produced by said second monomer composition has a glass transition temperature in the range of from about 15° C. to about 50° C.
18. An emulsion polymerization process according to claim 1 , wherein the polymer produced by said second monomer composition has a glass transition temperature in the range of from 17 to 78° C.
19. An emulsion polymerization process according to claim 1 , wherein the amount of the epoxy-functional, ethylenically unsaturated compounds or silicone-functional, ethylenically unsaturated compounds is from 0.7 weight percent to 5 weight percent.