Thermoplastic resin composition and molding form for same

1. A molded product comprising a thermoplastic resin composition comprising:

(A) about 10 wt % to about 60 wt % of a rubber-modified aromatic vinyl graft copolymer resin;

(B) about 10 wt % to about 60 wt % of a polyester resin;

(C) about 1 wt % to about 40 wt % of a maleimide-based polymer, wherein the maleimide-based copolymer (C) is a copolymer of an N-substituted maleimide, an unsaturated dicarboxylic acid anhydride, and a vinyl monomer;

(D) about 5 wt % to about 40 wt % of a modified aromatic vinyl compound-vinyl cyanide compound copolymer resin containing a functional group capable of reacting with polyester,

wherein the modified aromatic vinyl compound-vinyl cyanide compound copolymer resin (D) has a weight average molecular weight from about 50,000 g/mol to about 200,000 g/mol and

wherein the modified aromatic vinyl compound-vinyl cyanide compound copolymer resin (D) is a copolymer of about 0.01 mol % to about 5 mol % of (d1) an unsaturated compound represented by the following Formula 1 and (d2) about 95 mol % to about 99.99 mol % of a vinyl-based compound,

wherein in Formula 1, R 3 , R 4 and R 5 are each independently hydrogen (H), a C 1 ˜C 12 alkyl group or unsaturated alkyl group, a C 6 ˜C 14 aryl group, or a C 1 ˜C 12 alkyl-substituted aryl group or unsaturated alkyl-substituted aryl group; Y is an ether group (—O—), a carboxyl group (—O—[C═O]—, —[O═C]—O—), a C 1 ˜C 12 alkylene group, a C 6 ˜C 14 arylene group, or a C 1 ˜C 12 alkyl-substituted arylene group; when Y is an ether group or a carboxyl group, each of R 1 and R 2 is a C 1 ˜C 12 alkylene group, a C 6 ˜C 14 arylene group, or a C 1 ˜C 12 alkyl-substituted arylene group, and when Y is a C 1 ˜C 12 alkylene group or a C 6 ˜C 14 arylene group or alkyl-substituted arylene group, Y represents (R 1 —Y—R 2 ); x is 0 or 1; and Z is an epoxy group, a carboxylic acid group, an isocyanate group, an oxadiazol group, an amine group, or a hydroxyl group; and

(E) about 6 wt % to about 12 wt % of an aromatic vinyl resin which is a copolymer of an alkyl(meth)acrylate, aromatic vinyl compound, and vinyl cyanide,

wherein the molded product prepared by molding the thermoplastic resin composition has an average surface roughness (Ra) from about 10 nm to about 62 nm as measured using an optical profiler (NT1100).

2. The molded product comprising the thermoplastic resin composition according to claim 1 , wherein the polyester resin (B) is a recycled polyester resin.

3. The molded product comprising the thermoplastic resin composition according to claim 1 , wherein the maleimide-based polymer (C) has a weight average molecular weight from about 80,000 g/mol to about 200,000 g/mol.

4. The molded product comprising the thermoplastic resin composition according to claim 1 , wherein the maleimide-based polymer (C) comprises about 20 mol % to about 55 mol % of repeat units derived from maleimide.

5. The molded product comprising the thermoplastic resin composition according to claim 1 , wherein the (E) aromatic vinyl resin copolymerized with an alkyl(meth)acrylate has a weight average molecular weight from about 80,000 g/mol to about 200,000 g/mol.

6. The molded product comprising the thermoplastic resin according to claim 1 , wherein the molded product has a metal layer formed on a surface thereof.

7. The molded product comprising the thermoplastic resin composition according to claim 1 , wherein the (E) aromatic vinyl resin is a copolymer consisting of an alkyl(meth)acrylate, aromatic vinyl compound, and vinyl cyanide.