Method for producing homogeneously matted coatings by radiation curing
View Patent ↗The present invention relates to a method for producing matt and scratch-resistant coatings that takes place under exposure to actinic radiation on coating systems containing activated double bonds under radical polymerization.
1. A method for producing matt surfaces comprising:
(1) applying a radiation-curable coating agent to a substrate;
(2) irradiating the radiation-curable coating from step (1) with UV light having a wavelength from ≧200 nm to ≦420 nm in a radiation dose from 25 to 120 mJ/cm 2 ,
(3) irradiating the coating obtained from step (2) with UV light having a wavelength from ≧120 nm to ≦230 nm,
(4) finish-curing the coating obtainable from step (3) by actinic radiation.
2. The method according to claim 1 , wherein in step (2) the irradiation takes place with UV light having a wavelength from ≧280 nm to ≦420 nm.
3. The method according to claim 1 , wherein in step (3) the irradiation takes place with UV light having a wavelength from ≧150 nm to ≦225 nm.
4. The method according to claim 1 , wherein the radiation dose in step (2) is 30 to 100 mJ/cm 2 .
5. The method according to claim 1 , wherein the finish-curing in step (4) takes place with UV radiation at a wavelength from ≧200 nm to ≦420 nm in a radiation dose from 80 to 4000 mJ/cm 2 .
6. The method according to claim 1 , wherein the finish curing in step (4) takes place with electron beam radiation in a dose of 10 to 100 kGy.
7. The method according to claim 1 , wherein in step (1) the coating agent comprises:
a) one or more radiation-curable binders, and
b) one or more photoinitiators.
8. The method according to claim 7 , wherein the radiation-curable binder a) comprises an oligomer and/or polymer selected from the group consisting of (meth)acrylic copolymers, polyether (meth)acrylates, polyester (meth)acrylates, epoxy (meth)acrylates, urethane (meth)acrylates, amino (meth)acrylates, melamine (meth)acrylates, silicone (meth)acrylates and phosphazene (meth)acrylates.
9. The method according to claim 1 , wherein in step (1) the coating agent is applied to the substrate in a coating thickness from ≧5 μm to ≦650 μm.
10. The method according to claim 1 , wherein step (2) takes place under atmospheric conditions and step (3) takes place in an inert gas atmosphere.
11. A substrate coated by a method according to claim 1 .