Flame retardant structural epoxy resin adhesives and process for bonding metal members
View Patent ↗A heat-curable structural adhesive includes at least one non-rubber-modified epoxy resin; an optional rubber or toughener, one or more epoxy curing agents, one or more epoxy curing catalysts; and a flame retardant mixture that includes (i) alumina trihydrate, (ii) zinc borate and (iii) melamine or a melamine derivative. The structural adhesive is useful for bonding metals to other materials or metals to other metals. The structural adhesive strongly resists ignition when welding is performed in the presence of the uncured material, and does not interfere significantly with weld performance.
1. A heat-curable structural adhesive, comprising
A) at least one non-rubber-modified epoxy resin;
B) one or more epoxy curing agents;
C) one or more epoxy curing catalysts; and
D) a flame retardant mixture that includes (i) alumina trihydrate, (ii) zinc borate and (iii) melamine,
and the structural adhesive contains 4 to 12 weight percent contains alumina trihydrate and 1 to 8 weight percent each of zinc borate and melamine, and contains 14 to 25 weight percent combined of alumina trihydrate, zinc borate and melamine.
2. The heat-curable structural adhesive of claim 1 which contains 4 to 10 weight percent alumina trihydrate and 2 to 6 weight percent each of zinc borate and melamine, and contains 14.5 to 22 weight percent combined of alumina trihydrate, zinc borate and the melamine.
3. The heat-curable structural adhesive of claim 1 which contains 5 to 8 weight percent alumina trihydrate and 4 to 6 weight percent each of zinc borate and melamine, and contains 14.5 to 18 weight percent combined of alumina trihydrate, zinc borate and the melamine.
4. The heat-curable structural adhesive of claim 1 which further comprises:
E) (i) at least one rubber-modified epoxy resin, (ii) at least one core-shell rubber, (iii) at least one reactive elastomeric toughener containing capped isocyanate groups or a combination of any two or more thereof.
5. The heat-curable structural adhesive of claim 4 which has a total rubber content of from 4 to 18% by weight.
6. The heat-curable structural adhesive of claim 4 which contains from 10 to 25% by weight of the elastomeric reactive toughener.
7. The heat-curable structural adhesive of claim 1 which contains from 2 to 5% by weight calcium oxide.
8. The heat-curable structural adhesive of claim 1 wherein component C) includes 2,4,6-tris(dimethylaminomethyl)phenol integrated into a poly (p-vinylphenol) matrix or integrated into a novolac resin.
9. A process for bonding and welding metal members together, comprising the steps of
a) forming a layer of a heat-curable structural adhesive between and in contact with a pair of metal members to produce an uncured assembly;
b) welding the uncured assembly to form one or more welds between the pair of metal members; and then
c) heating the assembly to cure the structural adhesive and form an adhesive bond between the pair of metal member,
wherein the heat-curable structural adhesive comprises
A) at least one non-rubber-modified epoxy resin;
B) one or more epoxy curing agents;
C) one or more epoxy curing catalysts; and
D) a flame retardant mixture that includes (i) alumina trihydrate, (ii) zinc borate and (iii) melamine or a melamine derivative,
and the structural adhesive contains 4 to 12 weight percent contains alumina trihydrate and 1 to 8 weight percent each of zinc borate and melamine or melamine derivative, and contains 14 to 25 weight percent combined of alumina trihydrate, zinc borate and melamine or melamine derivative.
10. The process of claim 9 , wherein at least one of the metal members is steel.
11. The process of claim 9 , wherein the welding is performed by mid-frequency direct current welding.