Polybutylene terephthalate resin pellets, and production method for said polybutylene terephthalate resin pellets
View Patent ↗Provided is technology that causes polybutylene terephthalate resin to react with a reactive compound and reduces the thermal decomposition of the polybutylene terephthalate resin, when performing reactive processing method using the polybutylene terephthalate resin. During production of polybutylene terephthalate resin pellets, the polybutylene terephthalate resin (A) and a reactive compound (B) that reacts with the polybutylene terephthalate resin (A) are reacted such that the difference between the intrinsic viscosity of a polybutylene terephthalate resin composition configuring the polybutylene terephthalate resin pellets and the intrinsic viscosity of a polybutylene terephthalate resin composition configuring a polybutylene terephthalate resin molded article is no more than 0.05 dL/g, and the amount of carboxylic group ends in the resin included in the polybutylene terephthalate resin pellets is adjusted so as to be no more than 25 meq/kg.
1. A method of producing a polybutylene terephthalate resin pellet, comprising:
reacting a polybutylene terephthalate resin (A) and a reactive compound (B) that is reactive with the polybutylene terephthalate resin (A) in an extruder under production conditions satisfying the following inequality expression (I):
200≦(( T die −T m )×( T cylinder /T m ))/( Q/N s )≦300 (I)
wherein, T die represents resin temperature in degrees Celsius when the resin is discharged from a die, T cylinder represents cylinder temperature in degrees Celsius, Q represents extrusion output in kilograms/hour (kg/hr), Ns represents screw speed in revolutions per minute (rpm), and T m represents the melting point of the polybutylene terephthalate resin (A) in degrees Celsius and wherein the units on the bounds of the inequality are consistent with the above units.
2. The method of producing a polybutylene terephthalate resin pellet according to claim 1 , wherein the extruder is provided with a screw comprising, a supplying portion having a raw material-supply port, a plasticizing portion plasticizing a raw material conveyed from the supplying portion side, and a kneading portion kneading the raw material plasticized in the plasticizing portion, from the upstream side toward the downstream side in this order; and
the ratio of the kneading portion to the total length of the screw is 5% or more and 20% or less.