Method for preparing magnetic iron oxide
View Patent ↗A method for preparing magnetic iron oxide Fe 21.333 O 32 , comprising the following steps: (1) preparing a ferrous salt solution with solid soluble ferrous salt; (2) preparing a hydroxide solution; (3) mixing said hydroxide solution and said ferrous salt solution in a co-current manner for reaction at an alkali ratio of 0.6-0.8 and a reaction temperature not exceeding 30° C.; (4) after the reaction in step (3) is finished, yielding a first mixture, then charging said first mixture with a gas containing oxygen for oxidation, and controlling the first mixture at a pH value of 6-8 until the oxidation is finished to yield a second mixture; (5) filtering, washing with water and drying said second mixture obtained in step (4) to yield a precursor; and (6) calcining the precursor obtained in step (5) at 250-400° C.
1. A method for preparing magnetic iron oxide Fe 21.333 O 32 , comprising the following steps:
(1) preparing a ferrous salt solution with solid soluble ferrous salt;
(2) preparing a hydroxide solution;
(3) mixing said hydroxide solution and said ferrous salt solution in a co-current manner for reaction, controlling said hydroxide solution and said ferrous salt solution at an alkali ratio of 0.6-0.8, controlling said ferrous salt solution at a feeding speed of 200-300 ml/min, and said hydroxide solution at a feeding speed of 50-60 ml/min, and controlling the reaction temperature not exceeding 30° C.;
(4) after the reaction in step (3) is finished, yielding a first mixture, charging the first mixture with a gas containing oxygen for oxidation, and controlling the first mixture at a pH value of 6-8 until the oxidation is finished to yield a second mixture;
(5) filtering, washing with water and drying said second mixture to yield a precursor; and
(6) calcining the precursor obtained in step (5) at 250-400° C.
2. The method of claim 1 , wherein, the calcining temperature in step (6) is 300-350° C.
3. The method of claim 1 , wherein, said hydroxide is a hydroxide of group IA or group IIA elements.
4. The method of claim 1 , wherein, said ferrous salt solution has a concentration of 1.3-1.8 mol/L, and said hydroxide solution has a concentration of 4-6 mol/L.
5. The method of claim 4 , wherein, in step (4), controlling the first mixture at the pH value of 6-8comprises adding a further amount of hydroxide solution to the first mixture.
6. The method of claim 5 , wherein, in step (4), the further amount of hydroxide solution has a concentration of 4-6 mol/L and a feeding speed of 10-20 ml/min.
7. The method of claim 1 , wherein, in step (5), said drying is carried out at a temperature not exceeding 90° C.
8. The method of claim 1 , wherein, in step (4), water is added into the first mixture before charging the first mixture with a gas containing oxygen for oxidation.
9. The method of claim 1 , wherein, in step (4), the oxidation lasts for 10-15 h.
10. The method of claim 9 , wherein, in step (4), the gas containing oxygen is air, and the introduction amount of air is not less than 700 L/h.
11. The method of claim 2 , wherein, said hydroxide is a hydroxide of group IA or group IIA elements.
12. The method of claim 2 , wherein, said ferrous salt solution has a concentration of 1.3-1.8 mol/L, and said hydroxide solution has a concentration of 4-6 mol/L.
13. The method of claim 12 , wherein, in step (4), controlling the first mixture at the pH value of 6-8 comprises adding a further amount of hydroxide solution to the first mixture.
14. The method of claim 13 , wherein, in step (4), the further amount of hydroxide solution has a concentration of 4-6 mol/L and a feeding speed of 10-20 ml/min.
15. The method of claim 6 , wherein, the total alkali ratio of the hydroxide solutions, including that added for mixing with the ferrous salt solution and these that added for controlling the first mixture at the pH value of 6-8, to the ferrous salt solution is 1.05-1.25.
16. The method of claim 14 , wherein, the total alkali ratio of the hydroxide solutions, including that added for mixing with the ferrous salt solution and that added for controlling the first mixture at the pH value of 6-8, to the ferrous salt solution is 1.05-1.25.
17. The method of claim 2 , wherein, in step (5), said drying is carried out at a temperature not exceeding 90° C.
18. The method of claim 2 , wherein, in step (4), the oxidation lasts for 10-15 h.