Weather-proof thermoplastic moulding compounds with improved toughness on the basis of styrene copolymers and polyamides
A thermoplastic molding compound that has proved to be extremely weather-resistant and low-emission containing the following components: A) 3-77% by weight of one or more styrene copolymers, component A; B) 15-89% by weight of one or more polyamides, component B; C) 5-50% by weight of two or more graft rubbers without olefinic double bonds in the rubber phase, component C; D) 1-25% by weight of a terpolymer of styrene, acrylonitrile and maleic anhydride, component D; E) 2-30% by weight of rubber based on olefinic monomers, component E; F) 0-50% by weight of fibrous or particulate filler or mixtures thereof, component F; G) 0-40% by weight of further additives, component G.
1. A thermoplastic molding composition consisting essentially of the following components:
A) 3 to 77 wt % of one or more styrene copolymers, as component A,
B) 15 to 89 wt % of one or more polyamides, as component B,
C) 5 to 50 wt % of two or more graft rubbers without olefinic double bonds in the rubber phase, as component C, wherein the graft base core of the two or more graft rubbers is based on elastomers selected from the group consisting of elastomers based on C 1 to C 8 alkyl esters of acrylic acid, ethylene/propylene, or siloxanes,
wherein the two or more graft rubbers comprise a first graft rubber C1 and a second graft rubber C2, wherein:
the first graft rubber C1 has a graft shell comprising 60 to 95 wt % of styrene or α-methylstyrene or mixtures thereof and 5 to 40 wt % of at least one unsaturated nitrile, and
the second graft rubber C2 has a graft shell based on acrylates or methacrylates, and a fraction of 0.1 to 2 wt % of a monomer containing epoxide groups, in the outer graft shell,
D) 1 to 25 wt % of a terpolymer of styrene, acrylonitrile, and maleic anhydride, as component D,
E) 2 to 30 wt % of rubber based on olefinic monomers, as component E,
F) 0 to 50 wt % of fibrous or particulate filler or mixtures thereof, as component F,
G) 0 to 40% of further adjuvants, as component G,
the wt % being based in each case on the total weight of components A to G and together making 100 wt %.
2. The thermoplastic molding composition as claimed in claim 1 , consisting essentially of:
A) 10 to 70 wt % of one or more styrene copolymers, as component A,
B) 20 to 60 wt % of one or more polyamides, as component B,
C) 14 to 35 wt % of two or more graft rubbers without olefinic double bonds in the rubber phase, as component C, wherein the graft base core of the two or more graft rubbers is based on elastomers selected from the group consisting of elastomers based on C1 to C8 alkyl esters of acrylic acid, ethylene/propylene, or siloxanes,
D) 2 to 10 wt % of a terpolymer of styrene, acrylonitrile, and maleic anhydride, as component D,
E) 3 to 30 wt % of rubber based on olefinic monomers, as component E,
F) 0 to 50 wt % of fibrous or particulate filler or mixtures thereof, as component F,
G) 0 to 40% of further adjuvants, as component G,
where the mixture used as component C) consists of at least two different graft rubbers which differ in their graft shells, the first graft rubber of component C) having a graft shell of styrene and acrylonitrile, and the second graft rubber of component C) having a graft shell which comprises glycidyl methacrylate.
3. The thermoplastic molding composition as claimed in claim 1 , consisting essentially of:
A) 10 to 70 wt % of a SAN copolymer, as component A,
B) 20 to 60 wt % of one or more polyamides, as component B,
C) 14 to 35 wt % of two or more graft rubbers without olefinic double bonds in the rubber phase, as component C, wherein the graft base core of the two or more graft rubbers is based on elastomers selected from the group consisting of elastomers based on C1 to C8 alkyl esters of acrylic acid, ethylene/propylene, or siloxanes,
D) 2 to 10 wt % of a styrene-acrylonitrile-maleic anhydride terpolymer as component D,
E) 3 to 30 wt % of rubber based on olefinic monomers, as component E,
F) 0 to 50 wt % of fibrous or particulate filler or mixtures thereof, as component F,
G) 0 to 40% of further adjuvants, as component G,
where the mixture used as component C) consists of at least two different graft rubbers which differ only in their graft shells.
4. The thermoplastic molding composition as claimed in claim 1 , characterized in that the average particle diameter of component C is between 50 to 800 nm.
5. The thermoplastic molding composition as claimed in claim 1 , characterized in that two different rubber components are used as component C, at least one of the rubbers having a bimodal particle size distribution.
6. The thermoplastic molding composition as claimed in claim 1 , characterized in that the first graft rubber of component C has a graft shell of styrene and acrylonitrile, and the second graft rubber of component C has a graft shell which comprises glycidyl methacrylate.
7. The thermoplastic molding composition as claimed in claim 1 , characterized in that component B has from 0.05 to 0.5 wt % of triacetonediamine (TAD) end groups.
8. The thermoplastic molding composition as claimed in claim 1 , characterized in that it comprises two graft rubbers as component C), and the first graft rubber of component C) has a graft shell of styrene and acrylonitrile, and the second graft rubber has a graft shell which consists of glycidyl methacrylate and methyl methacrylate.
9. A process for producing thermoplastic molding compositions as claimed in claim 1 , characterized in that components A, B, C, D, and E, and also optionally F and G, are mixed with one another in any order at temperatures of 100 to 300° C. under a pressure of 1 to 50 bar and the mixture is subsequently kneaded and extruded.
10. A process for producing a thermoplastic molding composition, wherein the thermoplastic molding composition comprises the following components:
A) 3 to 77 wt % of one or more styrene copolymers, as component A,
B) 15 to 89 wt % of one or more polyamides, as component B,
C) 5 to 50 wt % of two or more graft rubbers without olefinic double bonds in the rubber phase, as component C, wherein the graft base core of the two or more graft rubbers is based on elastomers selected from the group consisting of elastomers based on C 1 to C 8 alkyl esters of acrylic acid, ethylene/propylene, or siloxanes,
D) 1 to 25 wt % of a terpolymer of styrene, acrylonitrile, and maleic anhydride, as component D,
E) 2 to 30 wt % of rubber based on olefinic monomers, as component E,
F) 0 to 50 wt % of fibrous or particulate filler or mixtures thereof, as component F,
G) 0 to 40% of further adjuvants, as component G,
the wt % being based in each case on the total weight of components A to G and together making 100 wt %,
wherein components A, B, C, D, and E, and also optionally F and G, are mixed with one another in any order at temperatures of 100 to 300° C. under a pressure of 1 to 50 bar and the mixture is subsequently kneaded and extruded, and
wherein a part of component D is first premixed with a part of component B to form a masterbatch in a ratio of 1:1 to 1:2 and said masterbatch is subsequently mixed with further components A, B, C, D, and E, and also optionally F and G, to give the thermoplastic molding composition.
11. Moldings, fibers, or foils comprising or consisting of a thermoplastic molding composition as claimed in claim 1 .