Low volatile organic component dry erase siloxane-based coatings
View Patent ↗The present invention provides, among other things, compositions with at least one dry-erase characteristic and methods thereof. In some embodiments, provided paint composition comprising a resin part comprising an epoxy, a polysiloxane and an organooxysilane; and a cure part comprising one or more amino-silanes; the resin part and the cure part being designed and selected such that, when combined together, they cure to form a surface coating that demonstrates at least one dry-erase characteristic.
1. A dry-erase paint composition, comprising:
a resin part comprising an epoxy, a polysiloxane and an organooxysilane;
a cure part comprising one or more amino-silanes;
the resin part and the cure part being designed and selected to have an amine to epoxy equivalent weight ratio in a range of about 1.3 to about 5.
2. The dry-erase paint composition of claim 1 , wherein the cure part further comprises a opacifying agent or pigment.
3. The dry-erase paint composition of claim 1 , wherein the cure part further comprises a catalyst.
4. The dry-erase paint composition of claim 1 , wherein the one or more amino-silanes comprises one or more members selected from the group consisting of 2-aminoethyl-3-aminopropyl methyldimethoxysilane, n-butyl-3aminopropyl trimethoxysilane, 3-aminopropyl methyldiethoxysilane, 3-aminopropyl triethoxysilane, 2-aminoethyl-3-aminopropyl trimethoxysilane or any combination thereof.
5. The dry-erase paint composition of claim 1 , wherein the resin part and the cure part, when combined together, cure to form a surface coating characterized by a dry-erase characteristic selected from the group consisting of an average surface roughness (Ra) of less than about 7,500 nm; a maximum surface roughness (Rm) of less than about 10,000 nm; a 60 degree gloss of higher than 70; a contact angle of less than about 150 degrees; a porosity of less than about 45 percent; an elongation at break of between about 10 percent and about 100 percent; a Sward hardness of greater than about 3; a Taber abrasion value of less than about 150 mg/thousand cycles; a sag resistance of between about 4 mils and about 24 mils, and combination thereof.
6. The dry-erase paint composition of claim 1 , wherein the resin part and the cure part, when combined together, cure to form a surface coating characterized in that, when its surface is written on with a marking material comprising a colorant and a solvent, the solvent comprising one or more of water, alcohols, alkoxy alcohols, ketones, ketonic alcohols, esters, acetates, mineral spirits, or mixtures thereof, the marking material can be erased from the surface of the write-erasable material to be substantially invisible for more than 100 cycles of writing and erasing at the same position.
7. The dry-erase paint composition of claim 1 , wherein the resin part and the cure part, when combined together, cure to form a surface coating characterized by a soak time of at least about 4.
8. The dry-erase paint composition of claim 1 , having volatile organic compounds (VOCs) of less than 140 g/L.
9. The dry-erase paint composition of claim 1 having VOCs of less than 100 g/L.
10. The dry-erase paint composition of claim 1 , wherein the resin part is in a first container and the cure part is in a second container.
11. A dry-erase product comprising:
a curable composition extending upon a substrate, the curable composition being comprised of a combination of:
a resin part comprising an epoxy, a polysiloxane and an organooxysilane; and
a cure part comprising one or more amino-silanes;
wherein the curable composition has an amine to epoxy equivalent weight ratio in a range of about 1.3 to about 5, and
wherein the curable composition is characterized in that it cures under ambient conditions to form a surface coating characterized by at least one dry-erase characteristic.
12. A method of forming a dry-erase product, the method comprising:
applying a composition of a paint composition to a substrate to form a coating that cures to provide a surface, wherein the paint composition comprises:
a resin part comprising an epoxy, a polysiloxane and an organooxysilane; and
a cure part comprising one or more amino-silanes;
the resin part and the cure part being designed and selected such that, when combined together as having an amine to epoxy equivalent weight ratio in a range of about 1.3 to about 5, they cure to form a surface that demonstrates at least one dry-erase characteristic.
13. A paint composition comprising:
a resin part comprising an epoxy, a polysiloxane and an organooxysilane;
a cure part comprising one or more amino-silanes, which one or more amino-silanes comprise a combination of 2-aminoethyl-3-aminopropyl trimethoxysilane and n-butyl-3-aminopropyl trimethoxysilane;
the resin part and the cure part being designed and selected such that, when combined together, they cure to form a surface that demonstrates at least one dry-erase characteristic.
14. The paint composition of claim 13 , wherein the paint composition has an amine to epoxy equivalent weight ratio in a range of about 1 to about 5.
15. The paint composition of claim 14 , wherein the dry-erase characteristic is selected from the group consisting of an average surface roughness (Ra) of less than about 7,500 nm; a maximum surface roughness (Rm) of less than about 10,000 nm; a 60 degree gloss of higher than 70; a contact angle of less than about 150 degrees; a porosity of less than about 45 percent; an elongation at break of between about 10 percent and about 100 percent; a Sward hardness of greater than about 3; a Taber abrasion value of less than about 150 mg/thousand cycles; a sag resistance of between about 4 mils and about 24 mils, and combination thereof.
16. The paint composition of claim 14 , wherein the surface coating is characterized in that, when its surface is written on with a marking material comprising a colorant and a solvent, the solvent comprising one or more of water, alcohols, alkoxy alcohols, ketones, ketonic alcohols, esters, acetates, mineral spirits, or mixtures thereof, the marking material can be erased from the surface of the write-erasable material to be substantially invisible for more than 100 cycles of writing and erasing at the same position.